用恒电流放电、循环伏安法和电化学阻抗谱（ＥＩＳ）研究了ＰＴＦＥ对泡沫型氢氧化镍电极电化学性能的影响，发现ＰＴＦＥ的存在会增加电极的电化学反应电阻，降低电极反应的可逆性，从而使得电极的放电电位及容量有所降低，所以在制作粘结式电极的过程中应尽量减少粘结剂的用量．
Research work was performed for the influences of PTFE on the electrochemical properties of foamtype Ni(OH)_2 electrodes by constant current discharge. CV and EIS method. Experimental results exhibit that the existence of PTFE would decrease the reversibility of electrode reaction and increase the reaction resistance of the electrode; thus lower the discharge potential and capacity, so PTFE should be added as little as possible during the preparation of pastetype electrodes.
KulcsarS，AghJ，FazekasAetal．Microstructureofplasticbondednickelelectrodes．J．PowerSources，1982，8：552阎杰，周震，李宇轩等．粘结剂PTFE含量对泡沫镍正极放电性能的影响．中国化学会第七届华北化学学术研讨会论文集，1996：83UnateME，FolquerME，VilcheJRetal．Theinfluencesofforeigncationsontheelectrochemicalbehaviorofthenickelhydroxideelectrode．J．Electrochem．Soc．，1992，139（10）：26974曹晓燕，周作祥，袁华堂等．Co对Ni（OH）2电极质子扩散行为的研究．电化学，1996，2（3）：3195GorensteinA，DeckerF，EstradaWetal．ElectrochromicNiOxHyhydratedfilms：Cyclicvoltammetryandacimpedancespectroscopyinaqueouselectrolyte．J．Electroanal．Chem．，1990，277：2776CoriganDA，BendertRM．Efectofcoprecipitatedmetalionsontheelectrochemistryofnickelhydroxidethinfilms：Cyclicvoltammetryin1mol／LKOH．J．Electrochem．Soc．，1989，136：7237藤山鸟昭等著，陈震，姚建年译．电化学测定方法．北京：北京大学出版社，1995，2048ArmstrongRD，CharlesEA．SomeaspectsoftheA．C．impedancebehaviorofnickelhydroxideandnickel／cobalthydroxideelectrodesinalkalinesolution．J．PowerSources，1989，27：159KulcsarS，HorvathP，CsathGetal．TheinternalresistanceofplasticbondedhighrateNielectrodes．J．PowerSources，1982，8：6110周伟航．电化学测量．上海：上海科学技术出版社，1985：136