本文采用锰盐微乳液中通氧气法成功制备了超细粉末ＭｎＯ２，对所得样品进行了化学分析，ＸＲＤ，ＴＥＭ测试，证明为γＭｎＯ２，平均粒径在纳米级范围内．再经恒电流放电，循环伏安，分形维数，交流阻抗等测试，发现在适当制备条件下所得纳米ＭｎＯ２具有良好的放电性能，并对此作了初步的理论探讨
A nanophase MnO 2 was synthesized using w/o microemulsion as reation media, The most favorable experiment conditions for the preparation of nm MnO 2 were researched. XRD,TEM,AC impedance, cyclic voltammetry etc. examinations were used to characterize the sample comparison with the classical MnO 2 (I.C.No.1EMD,electrolytic manganese dioxide). Sample shows that the crystal styucture of the synthesized samples are mainly γ MnO 2, with average particle size in the nanometer as shown by TEM. It was found that the discharge capacity of nm MnO 2 obtained is significantly higher than that of the I.C.No.1 EMD.
1王晓慧，王子忱，李熙等．超微粒MnO2的合成．吉林大学学报（自然科学版），1992（1）：992BachS，HenryM，BafierNetal．SolGelsynthesismanganeseoxides．J．SolidStateChem．，1990，88（2）：325～3333BachS．PereiraRamosJP，BafierNetal．BirnesitemanganesedioxidesynthesizedviaSolGelprocess：Anewrechargeablecathaticmaterialforlithiumbateries．ElectrochimActa，1991，36（10）：15954门传玲，夏熙．纳米级电极材料制备与电化学性质研究（Ⅰ）—溶胶凝胶法制备纳米级MnO2的性能．电池，1997，27（5）：2055陈龙斌，甘礼华，岳天仪等．微乳液反应制备αFe2O3超细粒子的研究．物理化学学报，1994，10（8）：7506Kordesch等编，夏熙等译，电池组（第一卷）．轻工出版社，1981：3967郭源，刘玲，夏熙．Thefratalbehaviorofmanganisedioxideelectrodeinalkalineelectrolyte．电池，1995，25（4）：153～1588ZhangHong，XiaXi．DifusionmodelandfilingmechanismofprotoninalkalineforMnO2．J．Electrochem．Soc．1989，136（10）：2771