The Study on the Performance of MCFC Matrix Prepared by Flow Cast

Expand
  • (Dalian Inst. of Chem. Phys., Chinese Acad. of Sci.,Dalian 116023

Received date: 1998-11-28

  Revised date: 1998-11-28

  Online published: 1998-11-28

摘要

用流铸法制备电池隔膜,工艺简单易行,膜的质量有保证且易重复.其平均孔半径为0.18um,孔隙率64.4%左右.在200mA/m2放电时,用此膜组装的MCFC电池的电压高达0.854V.其他电化学性能也达到90年代初世界水平.

本文引用格式

林化新, 衣宝廉, 李乃朝, 曲天锡, 张恩浚, 孔连英, 程英才 . 用流铸法制备MCFC隔膜的性能研究[J]. 电化学, 1998 , 4(4) : 406 -413 . DOI: 10.61558/2993-074X.2710

Abstract

The matrix for MCFC were prepared by flow cast technique which gives reproducible and reliable results. Its mean pore radius is about 0.18 μm, and the porosity is about 65%. The performance of MCFC stacked with this type of matrix is 0.854 V at 200 mA/cm 2.

参考文献

1MasonDM,VandvunanJ.ProductionofβLiAlO2.USAPat3998939,1976,12,212KinositaK,AckermanJP.Electrolyteforuseinfuelcel,USAPat4115632,1978,9,193BaumgartnerCE,DecarloVJ,GluglaPGetal.Moltencarbonatefuelcelelectrolyte,structurefabricationusingelectrophoreticdeposition.J.Electrochem.Soc.,1985,132:574GeneralElectricCompany.DOEcontractDEAC0280ET17019QuarterlyReportNo3,AugQct,19805李乃朝等.冷滚法制备熔融碳酸盐燃料电池用γLiAlO2隔膜.膜科学与技术,1997,17(2):24~296LacovangeloCD,PascoWD.Hotrolmiledelectrolyatestructureformoltencarbonatefuelcel.J.Electrochem.Soc.,1988,135:2217UnitedTechnologiesCorporation.DOEcontractDEACO1-19ET15440,QuarterlyReportNo.4,JulySept,19808InstituteofGasTechnology.EPRINorp108510Project40227,January,19849ArendtRH,CuranMJ.Alternatesynthesisofelectrolytematrixformoltencarbonatefuelcel.J.Electrochem.Soc.,1980,127:1660~166610林化新,衣宝廉,李乃朝等.熔融碳酸盐燃料电池隔膜的制备方法.中国专利,申请号:97111018.211BohmeO,LeidichFU,SalgeHJetal.Developmentofmaterialsandproductiontechnologiesformoltencarbonatefuelcels.Int.J.HgdrogenEnergy,1994,19(4):349~35512林化新,张恩浚,孔连英等.熔融碳酸盐燃料电池性能的研究.电池,1997,27(3):110~113