以 无机盐 和金属 醇 盐为 前 驱 物， 用 溶 胶—凝 胶 法 制 备了 Ｌｉ２ ＋ ｘ Ｇｄ ｘ Ｓｉ１ ＋ ｘ Ｏ３（ ｘ ＝ ０ ～０ ．１ ５） ，用 Ｄ Ｔ Ａ、 Ｔ Ｇ、 Ｘ Ｒ Ｄ、 Ｔ Ｅ Ｍ 及交 流阻谱等 技术对样 品的结 构、形 貌、粒 径及 离子 导电 性等 进行掺杂量 观察和 测试．结果 表明：其 固溶体形 成的掺 杂量范围 是０ ＜ ｘ ≤０ ．０９ ，在 掺杂 量范 围内， 样品电导率 随掺杂 量增加而 增高；粉 末样品的 平均粒 径为 ８０ ｎ ｍ ；与 传统 的固 相合 成 方法 相比 ，该 法可使样品 的生成 温度降低 ，离子导 电性得到 提高．

Li 2+x Gd xSi 1-x O 3( x =0～0.15) samples have been prepared by the Sol_Gel method. The power samples were characterized by DTA_TG, XRD and TEM. Ionic conductivity of the sinter was determined by means of A_C impedance measurements. The experimental results showed that the range of solid_solution was 0< x ≤0.09, while the conductivity of samples raised with increasing amount of Gd 2O 3 added, and average grain size of samples was 80 nm. In comparing with the samples by the conventional solid state reaction, the samples prepared by Sol_Gel method required lower temperature and presented higher ionic conductivity.