本文分析了地下结构物外加电流阴极保护用阳极的工况环境条件 ;并对各类阳极材料的性能特点进行了评述 ;探讨了埋地辅助阳极材料的发展与应用方向 .
The requirements of impressed current anodes for the protection of underground structures were presented in this paper according to the analysis of working conditions. The characteristics and performance of various anodes such as scrap steel, graphite, high silicon cast iron, magnetite, platinized anode, conductive polymer cable anode and mixed metal oxide anode were reviewed. The development trend of impressed current anodes for underground applications was also discussed.
[1] 米琪 ,李庆林等编著 .管道防腐蚀手册 [S].北京 :中国建筑工业出版社 ,1994,30 .
[2 ] TatumJoeF .Deepanodeinstallationsandmaterialsforcathodicprotectionandgrounding ,CorrsionControl_7thAPCCC[M].Vol.2 ,Beijing :InternationalAcademicPublishers ,1991,96 4.
[3] KroonDavidH .Cathodicprotectionanodesunderground[J].MaterialsPerformance ,1989,2 8(1) :17.
[4 ] KroonDavidH .,SchrieberCharlesF .Performanceofimpressedcurrentanodesforcathodicprotectionun derground[J].Corrosion/ 84,PaperNo.44 .NACE ,1984.
[5 ] 火时中编著 .电化学保护 [M].北京 :化学工业出版社 ,1988,5 9.
[6 ] 胡士信主编 .阴极保护工程手册 [S].北京 :化学工业出版社 ,1999,10 5 .
[7] W .V .贝克曼 ,W .施文克著 ,胡士信等译 .阴极保护手册 [S].北京 :人民邮电出版社 ,1990 ,16 7
[8] 福谷英二 .电气防食用难溶性电极について [J].防食技术 ,1978,2 7:5 83.
[9] LewisThomasH .Endeffectphenomena[J].Corrosion/ 78,PaperNo .16 3,NACE ,1978.
[10 ] JohnL .Piazza,Cathodicprotectionmaterialsevaluationbyopenholetestmethod[J].Corrosion/ 83,PaperNo .2 95 ,NACE ,1983.
[11] SYJ 36_89,埋地钢质管道强制电流阴极保护设计规范 [S].中华人民共和国石油行业标准 ,1990
[12 ] RajaniG .L .Moderntrendinimpressedcurrentanodesforcathodicprotection[J].Proc.6thMiddleEastCorrosionConf.Vol.1.Bahrain :1994:383.
[13] 佐藤荣一 .外部电源用电极材料について [J].防锖管理 ,1981,(11) :18.
[14] BerkeleyK .G .C .Anodesforcathodicprotection_oldandnew[J].Corrosion/84,PaperNo .48.NACE ,1984.
[15 ] LinderB .Magnetiteanodesforimpressedcurrentcathodicprotection [J].Corrosion/78,PaperNo .15 9.NACE ,1978.
[16 ] 福泽秀刀 .采用铂系电极的电化学保护法 [J].防锖管理 ,1985 ,(2 ) :40 .
[17] WarneM .A .Preciousmetalanodes_theoptionsforcathodicprotection[J].Corrosion/78,PaperNo .142 .NACE ,1978.
[18] BaboianR .Performanceofplatinumcoadcolumbiumimpressedcurrentanodesinfreshwater[J].MaterialsPerformance,1983,2 2 (12 ) :15
[19] BaboianR .Miniaturisedimpressedcurrentcorrosionprotectionsystems[J].PlatinumMetalsRev .,1986 ,30 (2 ) :6 3.
[2 0 ] DreymanE .W .Preciousmetalanodes:stateoftheart[J].Mat.Prot.andPerf.,1972 ,11(9) :17.
[2 1] BaboianR .Newdevelopmentsinplatinumtypeanodes[J].Corrosion/78,PaperNo .140 ,NACE ,1978.
[2 2 ] SlyPM .Newanodeforcorrosionprotection[J].PlatinumMetalsRev .,1980 ,2 4(2 ) :5 6 .
[2 3] TatumJoeF .Platinizedanodesincarbonaceousbackfills_anewdimension[J].Corrosion/78,PaperNo.141.NACE ,1978.
[2 4] LoweRA .Platinizedtitaniumasanodematerial[J].Mat.Prot.andPerf.,196 6 ,5 (5 ) :2 3.
[2 5 ] HayfieldPCS .Platinizedtitaniumelectrodesforcathodicprotection[J].PlatinumMetalsRev .,1983,2 7(1) :2 .
[2 6 ] PanHuibo.Anodesforimpressedcurrentcathodicprotection[J].RareMetalMaterialsandEngineering,1991,2 0 (4) :6 1.
[2 7] MarshallWF .Advantagesofcontinuousimpressedcurrentanodesinhighresistivitysoilenvironments[J].MaterialsPerformance ,1998,37(6 ) :18.
[2 8] XuLikun Aninvestigationonfailurebehaviourofmetaloxideanodes[J] CorrosionandProtectionTech nology(inChinese) ,1998,10 (6 ) :337.
[2 9] RedingJT .Performanceofmixedmetaloxideactivatedtitaniumanodesindeepgroundbeds[J].Corro sion/87,PaperNo.9.NACE ,1987.
[30 ] FranciscoMF ,LucianoPS .Silicon_ironanodesvs.mixedoxide_titaniumanodes:afieldcomparison[J].CorrosionPrevention&Control,1997,(2 ) :19.