本文采用XPS ,SEM ,XRD和电化学充放电测试研究了硼掺杂的中间相碳素微球 (MCMB)的结构和性能 .结果表明掺杂硼提高了MCMB的石墨化程度和晶粒尺寸 ,极大地改变了MCMB的形貌 .电化学充放电实验说明硼掺杂的中间相碳素微球嵌锂过程处于较高的电位 ,并有较大的不可逆容量
陈茂惠
,
吴国涛
,
朱光明
,
尤金跨
,
林祖赓
. 硼掺杂的中间相碳素微球 (MCMB)用作锂离子电池负极材料的性能及表征(英文)[J]. 电化学, 2001
, 7(3)
: 263
-269
.
DOI: 10.61558/2993-074X.1425
The anodic performances of boron doped and undoped mesocarbon microbeads(MCMBs) were comparatively studied and the structures were characterized by XPS,SEM,XRD and electrochemical measurements. It was found that boron doping samples greatly increased the degree of graphitization and the crystallite size,leading to quite different morphology. Electrochemical discharge/charge cycle tests indicate that lithium intercalation occurred at a little higher potential for the boron doped MCMBs, being attended by greater irreversible capacity loss.
[1] KimC ,FujinoT ,MiyashitaK ,etal.Microstructureandelectrochemicalpropertiesofboron dopedmesocar bonmicrobeads[J].J .Electrochem.Soc.,2000,147(4):1257~1264.
[2] KimC ,FujinoT ,HayashiT ,etal.StructuralandelectrochemicalpropertiesofpristineandB dopedmaterialsfortheanodeofLi ionsecondarybatteres[J].J .Electrochem.Soc.,2000,147(4):1265~1270.
[3] ChangYoungChul,SohnHunJoon,IsaoMochida,etal.Anodicperformancesofmesocarbonmicrobeads(MCMB)preparedfromsyntheticnaphthaleneisotropicpitch[J],Carbon,1999,37:1285~1297.
[4] EndoM ,KimC ,DresselhausMS ,etal.StructuralanalysisoftheB dopedmesophasepitch basedgraphitefibersbyramanspectroscopy[J].PhyRev.B ,1998,58:8991~8996.
[5] EndoM ,KimC ,MiyashitaK ,etal.RecentdevelopmentofcarbonmaterialsforLiionbatteries[J].Carbon,2000,38:183~197.
[6] TasumiK ,IwashitaN ,FujimotoH ,etal.Theinfluenceofthegraphiticstructureontheelectrochemicalchar acteristicfortheanodeofsecondarylithiumbatterie[J].J .Elecreochem.Soc.,1995,142:716~720.
[7] InabaM ,YoshidaH ,OgumiZ ,InsituRamanstudyofelectrochemicallithiuminsertionintomesocarbonmi crobeadsheat treatedofvarioustemperatures[J],J .Electrochem.Soc.,1996,143:2572~2578.
[8] HenningG .Diffusionofboroningraphite[J].J .Chem.Phy.,1965,42:1167~1172.
[9] ShirasakiT ,DerreA ,FlandroisS ,etal.Synthesisandcharacterizationofboron substituedcarbons[J].Car bon,2000,38:1461~1467.
[10] KanerRB ,KouvetakisJ,BartlettN ,etal.Boron carbon nitrogenmaterialsofgraphite likestructure[J].Mater.Res.Bull.,1987,22:399