本文讨论了增塑剂、剪切速率、不同含量和不同表面性质的二氧化硅对LBG(一种偏氟乙烯和六氟丙烯共聚物 )的丙酮溶液粘度的影响机理
赵胜亮
,
朱光明
,
吴国涛
,
王翠英
,
尤金跨
. SiO_2表面性质对LBG丙酮溶液体系粘度的影响[J]. 电化学, 2002
, 8(1)
: 22
-26
.
DOI: 10.61558/2993-074X.3275
LBG is a copolymer of vinylidene fluoride (VF2) and hexafluorpropylene (HFP), factors that influence the viscosity of the LBG solution such as the shear rate, plasticizer, the content of the fumed silica with different surface treatment are discussed in detail.
[1] TarasconJM ,GozdzAS ,SchmutzC ,etal.PerformanceofBellcore’splasticrechargeableLi ionbatteries[J].SolidStateIonics,1996,(86_88):49～54.
[2] DuPasquiermA ,WarrenPC ,CulverD ,FozdzAS ,AmatucciGG ,etal.PlasticPVDF_HFPlaminatespreparedbyaphase_inversionprocess[J].SolidStateIonics,2000,(135):249～257.
[3] ColinA .VincentLithiumbatteries:a50_yearperspective,1959_2009[J].SolidStateIonics,2000,(134):159～167.
[4] YuriaSaito,HiroshiKataoka,ClausioCapiglia,etal.IonicconductionpropertiesofPVDF_HFPtypegelpolymerelectrolyteswithlithiumimidesalts[J].J .Phys.Chem.B 2000,104:2189～2192.
[5] LiuPeikang,GaoFeng.Filmformingmethodmethodforlithiumionrechargeablebatteries[P].U .S .PatentNumber5,720,780.
[6] WangHong_peng,Huanghai_tao,stephanleL .WunderNovelmicroporouspoly(vinylidenefluoride)blendelectrolytesforlithium_ionbatteries[J].J.ElectrochemicalSociety,2000,147(8):2853～2861.
[7] SongJY ,WangYY ,WanCC .Conductivitystudyofporousplasticizedpolymerelectrolytesbasedonpoly(vinylidenefluoride)[J].J.ElectrochemicalSociety,2000,147(9):3219～3225.
[8] AntoniSGozdz,TintonFalls,CarolineNSchmutz,etal.Hybridlithium ionbatterypolymermatrixcomposi tions[P].U .S .Patent5,571,634.
[9] TeofilJesionowski,AndrzejKrysztafkiewiczInfluenceofsilianecouplingagentsonsurfacepropertiesofpre cipitatedsilicas[J].AppliedSurfaceScience,2001,172:18～32.
[10] J .JanardhanaReddy,N .Ravi,M .Vifayakumar.Asimplemodelforviscosityofpowderinfectionmoudlingmixeswithbindercontentpowdercriticalbindervolumeconcentration[J].J .EuropeCeramicSo ciety,2000,20:2183～2190