利用恒电流阴极还原法或电流脉冲法在聚苯胺膜、PATP膜、Au膜和ITO基体上制备了CdS纳米微粒膜 ,并对其结构和紫外_可见吸收等性质进行初步表征 .结果表明基体对CdS微粒膜的结构和性能具有较大的影响
CdS nanoparticle films were prepared on the PANI film,PATP film,Au film and ITO respectively by constant current deposition or current impulse method,and their structure and character were also studied.The results show that the substrates influence the structure and character of CdS particle film.
[1] SalataOV ,DobsonPL ,HullPJ ,etal.Fabricationofnanoparticlesembededinapolymerbygas_aerososreativeelectrostaticdepositiontechnique[J].ThinSolidFilms,1994,251:1.
[2] WangBH ,WangDJ ,CuiY ,etal.Light_inducedaggregationofnanocrystallineCdSasphotoelectrodesinphotoelectrochemicalcells(PECs)[J].Synth.Met.,1995,71:2239.
[3] PethkarS ,PatilRC ,KherJA ,etal.DepositionandcharacterizationlofCdSnanoparticledpolyanilinecompos itefilms[J].ThinSolidFilms,1999,349:105.
[4] SunLD ,FuXF ,WangMW ,etal.SynthesisofCdSnanocrystalwithincopolymer[J].J .Lumin.,2000,87_89:538.
[5] BalakrishnanKS ,RostogiAC .Electrodepositiontechniqueandpropertiesofsemiconductingcadmiumchalco genidethinfilmsfromaproticelectrdytes[J].ThinSolidFilms,1988,163:279.
[6] EdamuraT ,MutoJ.PreparationandpropertiesofelectrodepositedternaryCdSxSe1-x andZnCd1-xSfilms[J].ThinSolidFilms,1993,226:135.
[7] BaranskiAS ,FawcettWR ,MacDonaldAC ,etal.Thestructuralcharacterizationofcadmiumsulfidefilmsgrowbyathedicelectrodeposition[J].Electrochem.Soc.,1981,128:963.
[8] LuoJ ,LinXH ,WuLL ,etal.Insituelectronicspectroscopictechniquesforinterfacialelectrochemistry[J].Chem.ResearchinChineseUniv.,1996,12:270.
[9] SasikalaG ,DhanasekaranR ,SubramanianC .ElectrodepositionandopticalcharacterisationofCdSthinfilmsonITO_coatedglass[J].ThinSolidFilms,1997,302:71.
[10] YamaguchiKY ,YoshidaT ,SugiuraT .,etal.AnovelapproachforCdSthin_filmdepositionelectrochemicallyinducedatom_by_atomgrowthofCdSthinfilmsfromacidicchmicalbath[J].J .Phys.Chem.B ,1998,102:9677.
[11] NishinoJ ,ChataniS ,UotaniY ,etal.ElctrodepositionmethodforcontrolledformationofCdSfolmsfromaqueoussolutions[J].J .Electroanal.Chem.,1999,473:217.
[12] YoshidaT ,YamaguchiK ,KazitaniT ,etal.Atom_by_atomgrowthofcadmiumsulfidethinfilmsbyelectrore ductionofaqueousCd2+_SCN-complex[J].J .Electroanal.Chem.,1999,473:209.
[13] RoutkevitchD ,BigioniT ,MoskovitsM ,etal.ElectrohemicalfabricationofCdSnanowirearraysin poronsanodicaluminumoxidetemplates[J].J .Phys.Chem.,1996,100:14037.
[14] MaGH ,LiuY ,ZhangXT ,etal.StudyonphotoluminescenceoftheorganizedCdSnanoparticlessystem[J].Chemicalresearches.,1999,10(4):13.
[15] WangY ,HerronN .PhotoluminesceneceandrelaxationdynamicsofCdSsuperclustersinzeolites[J].J.Phys.Chem.,1988,92:4988
[16] ChestnoyN ,HarrisTD ,HullR ,etal.LuminesceneceandphotophysicsofCdSsemiconductorclustersthena tureoftheemittingelectronicstate[J].J .Phys.Chem.,1986,90:3393.
[17] LuoJ ,HuangHG ,ZhangHP ,etal.Studiesonphotoelectrochemistryofnano_particulateTiO2/PANI/PATPfilmonAuelectrodes[J].J .NewMat.Electrochem.Systems,2000,3:249.
[18] HuangHG ,LuoJ ,ZhangHP ,etal.ThephotoelectrochemistryofAu/PATP/PANIfilmelectrodeandAu/PATP/PANI/TiO2 filmelectrode[J].Chem.J .ChineseUniversities,2000,21:283.
[19] HuangHG ,ZhengZX ,LuoJ ,etal.ThephotoelectrochemistryofTiO2_polyanilinecompositefilm[J].Chi neseJournalofElectrochemistry,2001,7(1):102.
[20] HuangHG ,ZhangHP ,ZhengZX ,etal.TheeffectofpreparationconditiononthephotoelectrochemicalperformanceofboththePANIfilmandTiO2_PANIcompositefilmonAu[J].ChineseJournalofElectro chemistry,2001,7(2):155.
[21] HuangHG ,ZhengZX ,LuoJ ,etal.Internalphotoemissioninpolyanilinerevealedbyphotoelectrochemistry[J].Synth.Met.,2001,123/2:321