采用固相合成方法制备掺锶尖晶石型锂锰氧化物 ,通过X射线衍射法对材料的结构进行了表征 .结果表明 ,当掺入的锶含量较低时 ,得到的产物具有尖晶石结构特征 ,并表现出极佳的电化学性能 ,材料在充放电循环 90周次后仍能保持 95%的容量
Sr_doped spinel phase_LiSrxMn 2-x O4 was successfully prepared by solid_state method. Structural and electrochemical characterizations were carried out. Although Sr 2+ has a large ion radius_1.12 ,the spinel structure can be well maintained for LiSrxMn 2-x O4 sample as far as the x value doesn't surpass 0.05. Electrochemical study presents supporting evidence that doping the stoichiometric LiSrxMn 2-x O4 phase with Sr is an effective way to improve the cycleability of LiSrxMn 2-x O4 spinel material. A remarkable enhancement of the cycleability with retention of the initial capacity >90 % after 95 cycles was observed for the Sr_doped spinel.
[1 ] XIAYong＿yao ,ZHOUYun＿hong ,MasakiYoshio .Capacityfadingoncyclingof 4VLi/LiMn2 O4cells[J].J.Electrochem .Soc. ,1 997,1 44:2 593～ 2 6 0 0 .
[2 ] DongHYoung ,YoungJShin ,SeungMOh .Dissolutionofspineloxidesandcapacitylossesin 4VLi/LixMn2 O4Cells[J].J.Electrochem .Soc . ,1 996 ,1 43 :2 2 0 4～ 2 2 1 1 .
[3 ] GuohuaL ,IkutaH ,UchidaY ,etal,ThespinelphasesLiMyMn2 -yO4(M =Co ,Cr ,Ni)asthecathodeforrechargeablelithiumbatteries[J].J.Electrochem .Soc. ,1 996 ,1 43 :1 78～ 1 82 .
[4] AroraP ,PopovBN ,WhiteRE ,ElectrochemicalinvestigationofCobalt＿DopedLiMn2 O4ascathodematerialforlithium＿ionbatteries[J].J.Electrochem .Soc . ,1 9981 45:80 7～ 81 5.
[5] SUNYang＿Kook ,KIMDong＿Won ,ChoiYoung＿Min .SynthesisandcharacterizationofspinelLiMn2 -xNixO4forlithium/ polymerbatteryapplications[J].J.PowerSources,1 999,79:2 3 1～ 2 3 7.
[6 ] CrasFLe ,BlochD ,AnneM ,etal.LithiumintercalationinLi＿Mg＿Mn＿OandLi＿Al＿Mn＿Ospinels[J].SolidStateIonics,1 996 ,89:2 0 3～ 2 1 3 .
[7] CrasFLe ,BlochD ,AnneM ,etal.LithiumintercalationinLi＿Mg＿Mn＿OandLi＿Al＿Mn＿Ospinels[J].SolidStateIonics,1 996 ,89:2 0 3～ 2 1 3 .
[8] ChaCS ,LiCM ,YangHX ,etal.Powdermicroelectrodes[J].J .ElectroanalyticalChem . ,1 994,3 6 8:47～54