以阳极氧化铝膜 (AAO)作模板 ,制备聚苯胺 (PANI)纳米管和PANI纳米管列阵 ;同时利用溶胶_凝胶法制备ZnO_PANI同轴纳米线和同轴纳米线列阵 .PANI纳米管和ZnO_PANI同轴纳米线的形貌通过透射电子显微镜表征 .PANI纳米管的外径约 3 0nm ,内径约 1 0nm ;ZnO_PANI同轴纳米线直径约 60nm .实验发现 ,较之ZnO纳米线 ,同轴AAO模板中纳米线列阵的可见光发射谱带兰移 ,强度显著增强 ,这可能和PANI链上的NH基团与表面Zn2 +离子之间的相互作用有关 ,以及由于ZnO纳米微粒在PANI上富集、PANI的光生载流子部分转移给ZnO微粒所致 .实验还发现分散在NaOH溶液中的同轴纳米线 ,其可见光发射谱带比AAO模板中同轴纳米线的谱带兰移更甚
郑志新
,
席燕燕
,
董平
,
黄怀国
,
吴玲玲
,
林仲华
. ZnO-聚苯胺同轴纳米线及其列阵的制备和表征[J]. 电化学, 2002
, 8(2)
: 154
-159
.
DOI: 10.61558/2993-074X.1451
A novel nanomaterial,zinc oxide (ZnO) and polyaniline (PANI) coaxial nanowires and their array in the template,was synthesized using anodic aluminum oxide (AAO) membrane as template.The morphology of these coaxial nanowires was observed with transmission electron microscope (TEM).The experiments on photoluminescence (PL) of coaxial nanowires and their array in AAO membrane show that the visible emission band of ZnO shifts from 530 nm to 400 nm and the luminescence is enhanced for the coaxial nanowires array in AAO membrane,and the visible emission band shifts to a lower wavelergth(385 nm) for coatial nanowires in NaOH solution. Possible explanations for these two blue shifts of visible emission band of ZnO were presented.
[1] ZhangLi_de,MouJi_mei.NanomaterialsScience[M ].Shengyan:LiaoningScience&TechnologyPress,1994.
[2] LiuChao_feng,ZuYong,etal.Preparationandcharacteritationofnanosizezincoxide[J].ChemicalEngineer ingNewMaterials,1995,11:13.
[3] ZuYong,LiuChao_Feng,etal.Preparingnanositezincoxidebyhomogeneousprecipitation[J].ModernChemicalEngineering,1997,9:33.
[4] HuangMH ,MaoS ,FeickH ,etal.Room_temperatureUltravioletNanowireNanolasers[J].Science,2001,292:1897.
[5] KovtyukhovaNI ,GorchinskiyAD ,WarksaC .Self_assemblyofnanostructuredcompositeZnO/Polyanilinefilms[J].Mater.Sci.Eng,2000,B69_70:424.
[6] MasudaH ,SatohM .Fabricationofgoldnanodotarrayusinganodicporousaluminaasanevaporationmask[J].Jpn.J .Appl.Phys,1996,35:L126.
[7] MasudaH ,FukudaK .Orderedmetalnanoholearraysmadebyatwo_stepreplicationofhoneycombstructuresofanodicporousalumina[J].Science,1995,268:1466.
[8] MeulenkampEA .SynthesisandgrowthofZnOnanoparticles[J].Phys.Chem,1998,102:5566.
[9] MonticoneS ,TufeuR ,KanaevAVComplexnatureoftheUVandvisiblefluorescenceofcolloidalZnOnanoparticless[J].J .Phys.ChemB ,1998,102:2854.
[10] DijkenA ,MeulenkampEA ,VanmaekelberghD ,etal.TheluminescenceofnanocrystallineZnOparticles:themechanismoftheultravioletandvisibleemission[J].J.Lumin,2000,87_89:454