以工业废铁屑作原料制备高纯度电解铁,并优化了在氯化物溶液中的电解工艺条件,所得样品纯度最高可达到99.983%.通过SEM断面形貌观察,该电解铁样品非常致密.交流阻抗及腐蚀速率测定表明,电解铁的纯度越高,其耐腐蚀性能越好.
The high purity electrolytic iron was made from scrap iron chips. Electrolytic conditions of pure iron were determined in chloride baths and the highest purity was 99.983% by chemical analysis. Pure iron had very compact texture and high mechanical strength by SEM figures of cross section. In deaerated 0.5 kmol·m-3H2SO4 and 0.5 kmol·m-3NaCl solutions, the corrosion rate of iron decreased with increasing purity.
[1] AiLiuting,SongFulai,WangJianchao,etal.Proparation,propertiesandusesofelectrolyticpureiron[J].EngineeringChemistry&Metallurgy,1993,14:76～78.
[2] KunioTakada.Analysisofhighpurityiron-pastandpresent[J].BulletinoftheJapanofMetals,1990,29:267～268.
[3] FrankenthalRP,MilnerPC,SiconolfiDJ.Long-ternatmosphericoxidationofhighpurityiron[J].JournaloftheElectrochemicalSociety,1985,132:1019～1021.
[4] HiroshiKimura.Importanceofthepurificationforthefundamentalresearchofmetallicmaterials[J].BulletinoftheJapanInstituteofMetals,1994,33:3～4.
[5] SeiichiTakaki.Thecharacteristicsofultrahighpurityiron[J].BulletinoftheJapanInstituteofMet-als,1994,33:6～10.
[6] YinRenhe,LuKang,DaiYinchun,etal.InfluenceofinpuritiesCu,Zn,Snonelextrolyticproduction[J].EngineeringChenistry&Metallurgy,2000,21:183～186.
[7] YinRenhe,LuKang,CaoWeimin,etal.InfluenceofimpuritiesCo,Ni,Cdonelectrolyticproductionofhighpurityiron[J].JournalofEastChinaUniversityofScienceandTechnology,2000,26:183～187.