The Electrochemical Behavior of Amorphous Ni-P and Ni-B Alloys in 0.5 mol/L H_2SO_4

  • WANG Xu_cheng ,
  • WANG Wei_jiang ,
  • LIU Hou_tian ,
  • YU Zu_zhan
Expand
  • (Department of Chemistry, Fudan University, Shanghai 200433, China)

Received date: 2003-02-28

  Revised date: 2003-02-28

  Online published: 2003-02-28

摘要

应用极化曲线,交流阻抗等电化学测量方法分别研究了化学镀Ni-P和Ni-B合金电极在0.5mol/L硫酸溶液中的电化学行为,分析探讨了Ni,Ni-P和Ni-B合金三者在上述H2SO4溶液中其开路电位和阳极溶解特性差异的可能原因.

本文引用格式

王徐承 , 王卫江 , 柳厚田 , 郁祖湛 . 化学镀非晶态Ni-P和Ni-B合金在H_2SO_4溶液中的电化学行为[J]. 电化学, 2003 , 9(1) : 36 -40 . DOI: 10.61558/2993-074X.1481

Abstract

Polarization curves and impedance spectra were used to investigate the electrochemical behavior of amorphous Ni_P and Ni_B alloys in 0.5 mol/L H2SO4 solutions. The possible reason about the remarkable difference in the electrochemical behavior between amorphous Ni_P and Ni_B alloys was discussed.

参考文献

[1] JIANGXiaoxia,SHENWei.TheFundamentalandPracticeofElectrolessPlating[M].Beijing:Indus-tryofNationalDefencepress,2000.124~126. [2] GaevskayaTV,RakovichEV.Corrosion-electrochemicalbehaviorofelectrolessdepositednickel-boronfilms[J].Zashch.Met,1994,30(6),575~577. [3] ShvetsIB,LevinDM,ErusalimchikIG.Corrosionpropertiesofnickel-boronelectroplates[J].Za-shch.Met,1987,23(1):150~152. [4] WolfgangRiedel.ElectrolessNickelPlating(translatedbyLUOShoufu)[M].Shanghai:ShanghaiJiao-tongUniversityPress,1996.137~139. [5] DiegleRB,SorensenNR,NelsonGC.DissolutionofglassyNi-PalloysinH2SO4andHClelectrolytes[J].J.Electrochem.Soc.,1986,133,1769~1776. [6] DiegleRB,SorensenNR,ClaytonCR,etal.AnXPSinvestigationintothepassivityofanamor-phousNi-20Palloys[J].J.electrochem.Soc.,1988,135,1085~1092. [7] MarcusP,OdaO.Effectofphosphorusonthedissolutionandpassivationofnickelinanacidmedium[J].Mem.Sci.Rev.Metall.,1979,715. [8] KrolikowskiA,ButkiewiczP.AnodicbehaviorofNi-Palloysstudiedbyimpedancespectroscopy[J].ElectrochimicaActa,1993,38(14),1979~1983. [9] TohruWatanabe.AmorphousPlatinganditsApplications(translatedbyYUWeipingandLiDi)[M].Beijing:BeijingUniversityofAeronauticsandAstronauticspress,1992.121~128.