Oxidation Behavior of Zr-Cu-Al-Ni Amorphous Alloys in Air at 300～500 ℃

H. H. Hsieh ,
W. Kai ,
T. G. Neih ,
Y. Kawamura

Expand

( 1.Institute of Materials Engineering,Taiwan Ocean University,Keelung,20224,Taiwan,China,2.Lawrence Livermore National Laboratory, L_350, P. O. Box, Livermore, CA94551, USA,3.Department of Mechanical Engineering and Materials Science, Kumamoto University, Kumamoto 860_8555, Japan)

Received date: 2003-05-28

Revised date: 2003-05-28

Online published: 2003-05-28

Fold

摘要

本研究探讨锆基块状非晶质材料(Zr＿30Cu＿10Al＿5Ni)在空气中于300～500℃下之氧化行为.结果显示,非晶质合金之腐蚀动力学在300℃表现为直线型规律,350～425℃遵从抛物线型规律且氧化速率随温度上升呈现相对下降的趋势,但500℃时呈现复杂而不规则氧化行为.此外,非晶质合金氧化后生成的氧化物在300℃下皆为正方晶之ZrO2,当温度T≥350℃时,以正方晶结构之ZrO2为主,单斜晶之ZrO2和CuO次之.

关键词： 锆基非晶质材料; 氧化行为; 腐蚀动力学; ZrO2; CuO

本文引用格式

谢心心 , 开物 , 聂台刚 , 河村能人 . 锆基非晶质合金在300～500℃空气中之氧化行为研究[J]. 电化学, 2003 , 9(2) : 147 -155 . DOI: 10.61558/2993-074X.1498

Abstract

The oxidation behavior of the Zr_based bulk amorphous alloy (BMG; Zr_30Cu_10Al_5Ni in at.%) was studied in dry air over the temperature range 300～500 ℃. The kinetic results indicated that the amorphous alloy oxidized linearly at 300 ℃,while the parabolic oxidation was observed at 350～425 ℃, and the oxidation behavior at 500 ℃ was irregular and complicated. In general, the scales formed on the surface of the amorphous alloy were temperature_dependent, consisting of tetragonal_ZrO2 at 300　℃, and of mostly tetragonal_ZrO2 as well as minor amounts of monoclinic_ZrO2 and CuO at T≥350　℃.

参考文献

[1]　InoueA,ZhangT.FabricationofbulkglassyZr55Al10Ni5Cu30alloyof30mmindiameterbyasuctioncastingmethod[J].Mater.Trans.,JIM1996,37:185. [2]　InoueA,NishiyamaN,KimuraHM.ThermalstabilityandmagneticpropertiesofbulkamorphousFe＿Al＿P＿C＿B＿Sialloys[J].Mater.Trans.,JIM1997,38:189. [3]　ZhangT,InoueA,MasumotoT.AmorphousZr＿Al＿TM(TM=Co,Ni,Cu)alloyswithsignificantsupercooledliquidregionofover100K[J].Mater.Trans.,JIM,1998,32:1005. [4]　EckertJ,MatternN,ZinkevitchM,etal.CrystallizationbehaviorandphaseformationinZr＿Al＿Cu＿Nimetallicglasscontainingoxygen[J].Mater.Trans.,JIM,1998,39:623. [5]　DhawanA,RaetzkeK,FaupelF,etal.StudyofoxidationbehaviorofZr＿basedbulkamorphousalloyZr65Cu17.5Ni10All7.5bythermogravimetricanalyzer[J].Bull.Mater.Sci.,2001,3(24):281. [6]　SunX,SchneiderS,GeyerU,etal.OxidationandcrystallizationofanamorphousZr60Al15Ni25alloy[J].J.Mater.Res.,1996,11:2738. [7]　AsamiK,KimuraHM,HashimotoK,etal.HightemperatureoxidationofamorphousZr＿Nialloysinair[J].Mater.Trans.,JIM1995,36:988. [8]　BirksN,MeierG.IntroductiontoHigh＿temperatureOxidationofMetals[M].London:EdwardArnold,Ltd.,1983. [9]　DouglassDL.TheMetallurgyofZirconium.IAEA,Vienna,1971. [10]　KofstadP.HighTemperatureCorrosion[M],London＆NewYork:ElsevierAppliedScience,1988. [11]　GleesonB,DouglassDL,GesmundoF.ThecomprehensiveinvestigationofthesulfidationbehaviorofbinaryCo＿Moalloys[J].Oxid.Met.,1990,33:425.