以多孔阳极氧化铝为模板,采用两步交流电脉冲沉积法制备具有单晶结构的有序金纳米线阵列.实验表明:在氧化铝模板中由交流电沉积制备的金属纳米线,其成核电压直接影响模板内纳米线的填充率,而生长电压则控制纳米线的结构和形貌均一性.在最佳沉积条件下得到的金纳米线阵列,其填充率高达95%,且具有单晶结构.
The monocrystalline metal nanowire arrays were prepared by using a two-step AC electrodeposition in porous anodic aluminum oxide (AAO) template. The growth mechanism of nanowires was discussed. As a result, it has been found that the second voltage pulse has a considerable effect on the pore-filling ratio, the uniformity and the crystal structure, whereas the initial voltage pulse affects only the pore-filling ratio. Using the two-step AC electrodeposition, a highly ordered monocrystalline metal nanowire arrays with a pore-filling ration above 95% can be easily obtained.
[1] VinodPMenon,CharlesRMartin.FabricationandEvaluationofNanoelectrodeEnsembles[J].Anal.Chem.,1995,67:1920～1928.
[2] RoutkevitchD,TagerAA,HaruyamaJetal.Nonlithographicnano＿wirearrays:fabrication,physics,anddeviceapplications[J].IEEETransationsonElectronDevices.,1996,43(10):1646～1658.
[3] HellerA,AspnesDE,PorterJD.Transparentmetalspreparationandcharacterizationoflight＿transmittingplatinumfilms[J].Phys.Chem.,1985,89:4444～4452.
[4] WangZ,SuYK,LiHL.AFMstudyofgoldnanowirearrayelectrodepositedwithinanodicaluminumoxidetemplate[J].AppliedPhysicsA＿MaterialsScience＆Processing,2002,74(4):563～565.
[5] SauerG,BrehmG,SchneiderS.Highlyorderedmonocrystallinesilvernanowirearrays[J].J.Appl.Phys.,2002,91(5):3243～3247.
[6] PangYT,MengGW,ZhangLD,etal.ArraysoforderedPbnanowireswithdifferentdiametersindifferentareasembeddedinonepieceofanodicaluminamembrane[J].J.Phys.:Condens.Mater.,2002,14(45):11729～11736.
[7] LiMK,LuM,WangCW,etal.Preparationofwell＿alignedcarbonnanotubes/siliconnanowirescore＿sheathcompositestructurearraysinporousanodicaluminumoxidetemplates.ScienceinChinaSeriesB＿Chemistry.2002,45:435～444.
[8] NielschK,MullerF,LiAP,etal.Uniformnickeldepositionintoorderedaluminaporesbypulsedelectrodeposition[J].Adv.Mater.,2002,12:582～586.
[9] YinAJ,LiJ,JiangW,etal.Fabricationofhighlyorderedmetallicnanowirearraysbyelectrodeposition[J].Appl.Phys.Lett.,79,(2001)1039～1041.
[10] XuYF(徐云峰).OrderedmetalnanowirearraysfabricatedbyAAOtemplatemethodanditsstudyasSERSactivesubstrate[D].Xiamen:XiamenUniversity,2002.