Preparation of Photo-electrochemical Anticorrosion TiO_2 Films by Anodization Method

  • WU Peng-fei~ ,
  • LI Mou-cheng ,
  • SHEN Jia-nian ,
  • XIAO Mei-qun
Expand
  • (Institute of Materials, Shanghai University, Shanghai 200072, China

Received date: 2004-08-28

  Revised date: 2004-08-28

  Online published: 2004-08-28

摘要

应用阳极氧化法制备二氧化钛薄膜.研究了阳极氧化电压、电解质的性质、浓度对二氧化钛薄膜光电化学防腐蚀性能的影响,并测定该薄膜在模拟海水中的极化曲线以及与45#碳钢的耦合电流曲线.

本文引用格式

武朋飞 , 李谋成 , 沈嘉年 , 肖美群 . 阳极氧化法制备光电化学防腐蚀二氧化钛薄膜[J]. 电化学, 2004 , 10(3) : 353 -358 . DOI: 10.61558/2993-074X.3325

Abstract

Titanium oxide films have photo-electrochemical anticorrosion effect. We investigated the TiO_(2) films prepared by anodization method to protect for 45~(#) carbon steel in man-made seawater(3%NaCl). Various parameters, including voltages, electrolytes nature and concentration of electrolyte were examined. The polarization curves and of TiO_(2) and coupling photo-current curve between TiO_(2) film and 45~(#) carbon steel were measured.

参考文献

[1] OhkoY,SaitohS,TatsumaT,etal.Photoelectrochemicalanticorrosionandself cleaningeffectsofaTiO2coatingfortype304stainlesssteel[J].J.Electrochem.Soc.,2001,148(1):B24. [2] OhkoY,SaitohS,TatsumaT,etal.PhotoelectrochemicalanticorrosioneffectofSrTiO3forcarbonstee[J]J.ElectrochemicalandSolid StateLetters,2002,5(2):B9. [3] YuanJ,FujisawaR,TsujikawaS.PhotopotentialsofcoppercoatedwithTiO2bySol Gelmethod[J].Zairyo toKankyo,1994,43:433. [4] FujisawaR,TsujikawaS.Photo protectionof304stainlesssteelwithTiO2coating[J].MaterialsScienceForum.,1995,185188:1075. [5] YuanJ,TsujikawaS.CharacterizationofSol Gel DerivedTiO2coatingandtheirphotoeffectsoncoppersubstrates[J].J.Electrochem.Soc.,1995,142(10):3444. [6] YuanJ,TsujikawaS.Photo effectofSol GelderivedTiO2coatingoncarbonsteelinalkalinesolution[J].Zairyo toKankyo,1995,44:534. [7] HuangJ,ShinoharaT,TsujikawaS.ProtectionofcarbonsteelfromatmosphericcorrosionbyTiO2coating[J].Zairyo to Kankyo,1999,48:575. [8] HuangJ,ShinoharaT,TsujikawaS.EffectsofinterfacialironoxidesoncorrosionprotectionofcarbonsteelbyTiO2coatingunderillumination[J].Zairyo to Kankyo,1997,46:651. [9] AladjemA.Reviewanodicoxidationoftitaniumanditsalloys[J].JournalofMaterialsScience,1973,8:688. [10] Young TaegS,CarinaBJ,YongsooJ,etal.Theelectrochemicaloxidegrowthbehaviourontitaniuminacidandalkalineelectrolytes[J].MedicalEngineeringandPhysics,2001,23:329. [11] DelplanckeJL,DegrezM,FontanaA,etal.Self colouranodizingoftitanium[J].Surf.Technol.,1982,16:153. [12] JouveG,LeachJSL.Theincreaseintemperatureoftheanodicfilmformedontitaniumduringgrowthinacidmedia[J].ThinSolidFilms,1983,110:263. [13] ArsovLjD,KormannC,PliethW.InSituRamanSpectraofanodicallyformedtitaniumdioxidelayersinsolutionsofH2SO4,KOH,andHNO3[J].J.Electrochem.Soc.,1991,138(10):2964. [14] SatoN.Atheoryforbreakdownofanodicoxidefilmsonmetals[J].ElectrochimicaActa,1971,16:1683. [15] DyerCK,LeachJSL.Breakdownandefficiencyofanodicoxidegrowthontitanium[J].J.Electrochem.Soc.:ElectrochemicalScienceandTechnology,1978,125(7):1032.