Calcium Zincate Prepared by Ball Mill Method

  • LI Sheng-xian~ ,
  • TIAN Shuan-bao ,
  • ZHU Shao-shan
Expand
  • (College of Chemistry and Molecular Science, Wuhan University, Wuhan 430072, China

Received date: 2005-02-28

  Revised date: 2005-02-28

  Online published: 2005-02-28

摘要

应用球磨法制备锌酸钙,并研究制备过程的影响因素.XRD,TG DTA等测试表明,合成的锌酸钙化学组成为Ca(OH)2·2Zn(OH)2·2H2O.粉末微电极和模拟电池实验显示该材料具有良好的循环可逆性.

本文引用格式

李升宪 , 田拴宝 , 朱绍山 . 球磨法制备锌酸钙研究[J]. 电化学, 2005 , 11(1) : 72 -76 . DOI: 10.61558/2993-074X.1617

Abstract

Calcium zincate was prepared by ball milling method and the factors that influence its synthesis were investigated. The composition of the compound was Ca(OH)_2·2Zn(OH)_22H_2O, which was verified by XRD and TG-DTA methods. The results of powder microelectrode and in simulated batteries showed that the material had excellent cyclic performance.

参考文献

[1] RoyFThornton,EricJCarlson.Propertiesofalternateelectrolytesforsecondaryzincbatteries[J].J.Electro chem.Soc.,1980,127(7):1448~1455. [2] ChenJern shing,FrankRMclarnon,EltonJCairns.Investigationsoflow zinc solubilityelectrodesandelec trolytesinzinc/silveroxidecells[J].J.PowerSources,1992,39:333~348. [3] McBreenJ,GannonE.Theelectrochemistryofmetaloxideadditionsinpastedzincelectrode[J].Electro chimicaActa,1981,26(10):1439~1446. [4] ShivkumarJ,ParuthimalKalaignanG,VasudevanT.Studieswithporouszincelectrodeswithadditivesforsecondaryalkalinebatteries[J].J.PowerSources,1998,75:90~100. [5] SatoY,KaudaM,NikiH, etal.Longlifesealednick el zinccellusinganewseparator[J].J.PowerSources,1983,9:147~159. [6] FrankRMclarnon,EltonJCairns.Thesecondaryalka linezincelectrode[J],J.Electrochem.Soc.,1991,138(2):645~664. [7] JainR,AlderTC,MclarnonFR,etal.Developmentoflong livedhigh performancezinc calcium/nikeloxidecell[J].J.AppliedElectrochemistry,1992,22:1039~1048. [8] Charkey,Allen,Coates, etal.Calcium zincateelec trodeforalkalinebatteriesandmethodeformakingsame[P].USPatent:5863676,1999.