以GBL/EC复配体系为增塑剂, PVDF HFP和PMMA为聚合物基体制备胶态聚合物电解质. 研究聚合物电解质的离子传输特性和电化学稳定性. 实验表明,室温离子电导率达到 1. 2mS·cm-1, 电化学稳定窗口在 4. 5V以上. 以GBL/EC增塑聚合物电解质与表面经修饰的锂金属电极组成锂金属聚合物电池,其电极稳定性较好,充放电循环寿命得到很大的提高.
Polymeric gel electrolytes (GPE) based on PMMA and PVDF-HFP were prepared using the binary mixtures of γ-butyrolactone (GBL) and ethylene carbonate (EC) as plasticizers. The ionic transport properties and electrochemical stability were studied. The room temperature conductivity reached 1.2 mS·cm~(-1), electrochemical stability window exceeded 4.5V. The interfacial stability between GPE and lithium electrode was also investigated. The lithium metal polymer battery (LMPB) prepared with the GPE showed better charge and discharge life cycle when the the lithium metal electrode was treated with 1,4-dioxane.
[1] JayathilakaPARD,DissanayakeMAKL,AlbinssonI, etal.Dielectricrelaxation, ionicconductivityandthermalstudiesofthegelpolymerelectrolytesystemPAN/EC/PC/LiTFSIJ[J].SolidStateIonics,2003,56:179~195.
[2] DeepaM,SharmaN,AgnihotrySA.FTIRinvestigationsonion ioninteractionsinliquidandgelpolymericelectrolytes:LiCF3SO3PC PMMA[J].JournalofMa terialsScience,2002,37:1759~1765.
[3] ChagnesA,CarreB,WillmannP, etal.Modelingvis cosityandconductivityoflithiumsaltsinγ butyrolac tone[J].JournalofPowerSources.2002,109:203~213
[4] KikukoHayamizu,YuichiAihara,ShigemasaArai, etal.Diffusion, conductivityandDSCstudiesofapolymergelelectrolytecomposedofcross linkedPEO,γ butyro lactoneandLiBF4[J].SolidStaticIonics.1998,107:1~12
[5] YuichiAihara,ShigemasaArai,KikukoHayamizu.I onicconductivity,DSCandselfdiffusioncoefficientsoflithium, anion, polymer, andsolventofpolymergele lectrolytes: thestructureofthegelsandthediffusionmechanismoftheions[J].ElectrochimicaActa.2000,45:1321~1326.
[6] CaillonCaravanierM,ClaudeMontignyB,LemordantD, etal.Conductivitystudyofdiacrylate basedgelsPartIII.Influenceofthenatureoftheconstituentsandimprovementofatheoreticalmodelofionictransport[J].SolidStateIonics2003,156:113~127.
[7] ZhangSS,XuK,JowTR.Li ioncellwithpoly(acry lonitrile methylmethacrylate) basedgelpolymerelec trolyte.SolidStateIonics[J].2003,158:375~380.
[8] JamesEvans,ColinAVincent.Electrochemicalmeas urementoftransferencenumbersinpolymerelectrolytes.Polymer[J].1987,28:2324~2328.