锂离子电池过充特性的研究

  • 庞静 ,
  • 卢世刚
展开
  • 北京有色金属研究总院,北京有色金属研究总院,北京有色金属研究总院 北京100088,北京100088,北京100088

收稿日期: 2005-11-28

  修回日期: 2005-11-28

  网络出版日期: 2005-11-28

A Study of Overcharge Characteristic of Lithium-ion Cells

  • PANG Jing ,
  • LU Shi-gang~
Expand
  • (General Research Institute for Nonferrous Metals,Beijing 100088,China

Received date: 2005-11-28

  Revised date: 2005-11-28

  Online published: 2005-11-28

摘要

以尖晶石锰酸锂作锂离子电池正极材料,研究其过充电特性及影响因素.结果表明,电池1C过充特性和正极活性物质的量有关,与负极活性物质的量无关.充电倍率是影响电池过充特性的关键因素,低倍率过充时,结束电池过充的主要原因是内部电解液分解殆尽;高倍率过充时,因电池内部产生的热量增加,散热相对滞后,导致电池内部温度升高隔膜熔断从而截断回路结束过充.

本文引用格式

庞静 , 卢世刚 . 锂离子电池过充特性的研究[J]. 电化学, 2005 , 11(4) : 398 -401 . DOI: 10.61558/2993-074X.1675

Abstract

The overcharge characteristics and effect factors of lithium-ion cells containing LiMn_(2)O_(4)cathodes were studied in detail.Overcharge testing of Lithium-ion cells with a systematic variation in the cell balance demonstrated that the overcharge characteristics of Lithium-ion cells was affected by the amount of cathode in the cells,which is independent of the amount of anode material.The rate of charge was found to be an important parameter,as electrolyte complete decomposition at low charge rates caused the end of overcharge testing,while high charge rates accelerated the rate of heat generation in the cells and the cell temperature increased as a result of insufficient heat dissipation.The cell temperature rise led to the separator shut down and testing end.

参考文献

[1]M acNe il D D.A comparison of the electrode/electrolytereaction at elevated temperature for various L i-ion bat-tery cathodes[J].Journal of Power Sources,2002,108:8~14. [2]M acNe il D D.Comparison of the reactivity of variouscarbon E lectrodes w ith E lectrolyte at E levated Tempera-ture[J].Journal of the electrochem ical soc iety,1999,146(10):3 596~3 602. [3]Hosse in M alek i.Therm al stab ility stud ies of L i-ioncells and component[J].Journal of the electrochem i-cal soc iety,1999,146(9):3224~3229. [4]R ichard M N.Accelerating rate calorim etry study ontherm al stab ility of lith ium intercalated graph ite in elec-trolyte[J].I.Experim ental Journal of the E lectrochem-ical Soc iety,1999,146(6):2 068~2 077. [5]Hosse in M alek i.Therm al stab ility stud ies of b inder m a-terials in anode for L ithu im-ion batteries[J].Journalof the E lectrochem ical Soc iety,2000,147(12):4 470~4 475. [5]Tetsuya Kawamura.Therm al stab ility of alkyl carbonatesm ixed-solvent electrolytes for lith ium ion cells[J].Journal of Power Sources,2002,104:260~264. [6]Sh in-ich i Tob ish im a.A consideration of lith ium cellsafety[J].Journal of Power Sources,1999,81~82:882~886. [7]Kensh in K itoh.100W h large size L i-ion batteries andsafety tests[J].Journal of Power Sources,1999,81~82:887~890. [8]Spotn itz R,Franklin J.Abuse behavior of h igh-power,lith ium-ion cells[J].Journal of Power Sources,2003,113:81~100.