The Effect of Solution Concentration on Properties of Ru-Ti-Ir Oxide Anode Coatings

  • WANG Ke~
Expand
  • (1,2),HAN Yan~(1),WANG Jun-tao~(*1),ZHANG Xiao-ling~(2),SUN Yu-pu~(2)(1.State Key Laboratory for Marine Corrosion and Protection,Qingdao Branch of Luoyang Ship Material Research Institute,Qingdao 266071,Shandong,China,2.Department of Material Science and Engineering of Shandong University,Jinan 250061,Shandong,China

Received date: 2006-02-28

  Revised date: 2006-02-28

  Online published: 2006-02-28

摘要

应用热分解法制备了由不同浓度涂液形成的Ru-Ti-Ir氧化物阳极涂层,SEM,EDX,XRD、强化电解寿命、极化曲线、循环伏安和电化学阻抗等测试表明,涂液浓度对阳极涂层的表面形貌有着很大的影响,但不甚影响其析氯极化过程.随着涂液浓度的增加,阳极涂层的伏安电量和双电层电容都出现先降低后增加的变化趋势.

本文引用格式

王科 . 涂液浓度对Ru-Ti-Ir氧化物阳极涂层性能的影响[J]. 电化学, 2006 , 12(1) : 74 -79 . DOI: 10.61558/2993-074X.1702

Abstract

The anode coatings of Ru-Ti-Ir oxide with various solution concentrations were prepared by thermal decomposition.The scanning electron microscope(SEM),energy dispersive X-ray detector(EDX),X-ray diffraction(XRD),accelerated life,polarization curve,cyclic voltammetry and electrochemical impedance.spectroscopy(EIS)tests were carried out.The results showed that there was an obvious effect of solution concentrations on the morphology of the coatings,but little effect on polarization of chlorine evolution.Voltammetric charges and double layer capacitances of anode coatings had a tendency to fall down firstly then increase afterwards as the solution concentration increased.

参考文献

[1]Traeatti S.E lectrocatalysis:understand ing the success ofDSA[J].E lectroch im ica Acta,2000,45:2377~2385. [2]Ryu ich i O togawa,M aaatsugu morim itsu,Morio M atsuna-ga.E ffects of m icrostructure of IrO2-based anodes onelectrocatalytic properties[J].E lectroch im ica Acta,1998(44):1510. [3]Yosh io Takasu,Satosh i Onoue,Koh ich i Kam eyam a,etal.Preparation of u ltrafine RuO2-IrO2-TiO2oxide parti-c les by solgel process[J].E lectroch im ica Acta,1994,39(13):1996. [4]Cam ara O R,Trasatti S.Surface electrochem ical prop-erties ofTi/(RuO2+ZrO2)electrodes[J].E lectroch im-ica Acta,1996,41(3):420. [5]Trasatti S.Physical electrochem istry of ceram ic oxide[J].E lectroch im.Acta,1991,36(2):225. [6]Xu L K,Scantlebury J D.A study on the deactivation ofan IrO2Ta2O5coated titan ium anode[J].Corrosion Sc i-ence,2003,45:2734. [7]Kerner Z,Pajkossy T.On the origin of capac itance d is-persion of rough electrodes[J].E lectroch im ca.Acta,2000,46:207.