Electroless Nickel Plating on Carbon Nanotube with Non-palladium Activation Procedure

  • HUGuang-hui ,
  • WUHui-huang~ ,
  • YANGFang-zu
Expand
  • (College of Chemistry and Chemical Engineering,State Key Laboratory of Physical Chemistry of Solid Surfaces,Xiamen University,Xiamen 361005,Fujian,Chnia

Received date: 2006-02-28

  Revised date: 2006-02-28

  Online published: 2006-02-28

摘要

本文提出碳纳米管表面无钯活化的化学镀镍方法.碳纳米管经硝酸氧化和碱中和后表面生成羧基,利用羧基吸附镍离子,之后吸附的镍离子被化学还原为镍的纳米微粒并成为化学镀镍的催化活性中心.红外吸收光谱和电子显微镜观察等证实了上述活化过程的机理.实验表明,新的活化方法对碳纳米管表面化学镀是切实可行的,文中同时对化学沉积层的不同形貌进行讨论.

本文引用格式

胡光辉 , 吴辉煌 , 杨防祖 . 碳纳米管表面的无钯活化化学镀镍研究[J]. 电化学, 2006 , 12(1) : 25 -28 . DOI: 10.61558/2993-074X.1692

Abstract

A new procedure of surface activation without using palladium salt was proposed for electroless nickel plating on carbon nanotubes.In the procedure,carbon nanotubes were oxidized by nitric acid and then neutralized with NaOH to create carboxyl surface groups which were used to adsorb Ni~(2+)ions,thereafter the adsorbed Ni~(2+)ions were chemically reduced into Ni nano-particles as a catalytic center for electroless nickel deposition,all these were further confirmed by infrared absorption spectra and electron microscopic observations.The results indicate that the procedure is feasible to electroless nickel plating on carbon nanotubes.The different morphology of deposits obtained from electroless plating was also discussed.

参考文献

[1]W ong E W,Sheehan P E,L ieber C M.Nanobeam m e-chan ics:elastie ity,strength and toughness of nanorodsand nanotubes[J].Sc ience,1997,277:1 971~1 975. [2]TreacyM M J,Ebbesen TW,G ibson J M.Exception-ally h igh Young’s modu lus observed for ind ividual car-bon nanotubes[J].Nature,1996,381:678~680. [3]Tu J P,Yang Y Z,W ang L Y,et al.Tribological prop-erties of carbon nanotube re inforced copper composites[J].Tribol.Lett.,2001,10:225~228. [4]Dong S R,Tu J P,Zhang X B.An investigation of theslid ing wear behavior of Cu-m atrix composite re inforedby carbon nanotubes[J].M ater.Sc i.Eng.A,2001,313:83~87. [5]M a R Z,W u J,W e i B Q,et al.Processing and proper-ties of carbon nanotubes-nano-S iC ceram ic[J].J.M a-ter.Sc i.,1998,33:5 243~5 246. [6]Chen W X,Tu T P,Gan H Y,et al.E lectroless prepa-ration and tribological properties of N i-P-CNT compositecoatings under lubricated cond ition[J].Surf.Coat.Techn.,2002,160:67~83. [7]Chen X H,X ia J T,Peng J C,et al.Carbon-nanotubem etal-m atrix composites prepared by electroless p lating[J].Composites Sc ience and Technology,2000,60:301~306. [8]Ang L M,Hor T S A,Xu G Q,et al.Decoration of ac-tivated carbon nanotubes w ith copper and n ickel[J].Carbon,2000,38:363~372. [9]Dean J A.Lange’s Handbook of Chem istry[M].15 thEd.M cG raw-H ill Book Co.1999. [10]Bernhard Schroder.Ram an/Infrared Atlas of O ragan icCompounds[M].Second Ed ition.W e inhe im:VCH-Verl.-Ges.,1989. [11]Pe i Z F,Ponec V.On the interm ed iates of the aceticac id reactions on oxides:an IR study[J].App liedSurface Sc ience,1996,103:171~182. [12]Deacon G B,Ph illips R J.Relationsh ips between thecarbon-oxygen stretch ing freqenc ies of carbon oxylatocomp lexes and the type of carboxyliate coord ination[J].Coord ination Chem istry Reviews,1980,33:227~250. [13]Chen W X,Tu J P,Gan HY,et al.E lectroless prep-aration and tribological properties ofN i-P-Carbon nano-tube composite coatings under lubricated cond ition[J].Surface and Coatings Technology,2002,160:68~73.