应用两步化学还原法制备不同厚度的AucorePtshell纳米粒子,经紫外可见光谱(UV-V is)、透射电子显微镜(TEM)表征.该金纳米颗粒经化学还原包裹铂后平均粒径明显增大,调节金与铂的含量可获得不同包裹厚度的AucorePtshell纳米粒子.循环伏安法研究表明,粒径为70~80 nm的AucorePtshell纳米粒子对甲醇的氧化具有较好的电催化活性,并且其电催化性能随着电位循环扫描次数的增加而增强.
鲍芳
,
姚建林
,
顾仁敖
. Au_(core) Pt_(shell)纳米粒子对甲醇氧化的电催化性能研究[J]. 电化学, 2006
, 12(2)
: 218
-222
.
DOI: 10.61558/2993-074X.1726
Au_(core)Pt_(shell)nanoparticles with different thicknesses were prepared by using chemical reduction method,and characterized by ultraviolet-visible spectroscopy(UV-Vis),transmission electron microscopy(TEM) and cyclic voltammetry(CV).The electrocatalytic activity of Au_(core)Pt_(shell)nanoparticles with the mean diameter of 70~80 nm to methanol oxidation was investigated by cyclic voltammetry in the acid solution.The results revealed that the prepared core-shell nanoparticles were covered by Pt shell and exhibited the similar optical property and electrocatalytic activity with the normal Pt surface.Moreover,the electrocatalytic activity increased with the electrochemical sweep in the certain potential range.It might be contributed by the special loose structure of Pt shell rather than the increase of the real area.
[1]Golab i S M,Nozad A.E lectrocatalytic oxidation ofm eth-anol on electrodes mod ified by p latinum m icropartic lesd ispersed into poly(o-phenylened iam ine)film[J].J.E lectroanal Chem.,2002,521:161.
[2]M ikhaylova A A,Khazova O A.E lectrocatalytic and ad-sorption properties of p latinum m icropartic les electrode-posited onto glassy carbon and into Nafion film s[J].J.E lectroanal.Chem.,2000,480:225.
[3]Chen C W,Takezako T,Yam amoto K.Poly(N-vinyli-sobutyram ide)-stab ilized p latinum nanopartic les:syn-thesis and temperature-responsive behavior in aqueoussolution[J].Colloids and Surfaces A,2000,169:107.
[4]Hengle in A.Preparation and optical absorption spectraof Au/sub core/Pt/sub shell/and Pt/sub core/Au/subshell/colloidal nanopartic les in aqueous solution Phys[J].J.Chem.B,2000,104:2201.
[5]Lu L H,W ang H S,X i S Q,et al.Improved size con-trol of large pallad ium nanopartic les by a seed ing growthm ethod Journal of M aterials Chem istry[J].J.M ater.Chem.,2002,12:156.
[6]Sronova Sloufova L,Ledn icky F,Gemperle A.Core-Shell(Ag)Au b im etallic nanopartic les:analysis ofTransm ission electron m icroscopy Im ages[J].Lang-mu ir,2000,16:9928.
[7]Lu Lehu i,Sun Guoying,Zhang Hongjie.Fabrication ofcore-shell Au-Pt nanopartic le film and its potential ap-p lication as catalysis and SERS substrate[J].J.M ater.Chem.,2004,14:1005.
[8]Lu Lehu i,W ang Haishu i,X i Sh iquan,et al.Improvedsize control of large pallad ium nanopartic les by a seed inggrowth m ethod Journal of M aterials Chem istry[J].J.M ater.Chem.2002,12:156.
[9]Tian Na(田娜),ChenW e i(陈卫),Sun Sh i-Gang(孙世刚).Spectroscop ic characterization and electrocatalyticproperties of core-shell Au-Pt nanopartic les[J].ActaPhys.-ch im.S in.,2005,21:74.
[10]L i Jian-Feng(李剑锋),Hu Jia-W en(胡家文),RenB in(任斌),et al.Tun ing the SERS activity of Au-PdCore-shellNanopartic les by controlling the th ick iness ofthe Pd shell[J].Acta Phys.-Ch im.S in ica,2005,21:825.
[11]Frens G.Controlled nuc leation for the regu lation of thepartic le size in monod isperse gold suspensions[J].Nature,1973,241:20.
[12]Cre ighton J A,Eadon D G.U ltraviolet-visib le absorp-tion spectra of the colloidal m etallic elem ents[J].J.Chem.Soc.,Faraday Trans.,1991,87:3881.
[13]Teran ish i T,HosoeM,Tanaka T,et al.S ize control ofmonod ispersed Pt nanopartic lesand the ir 2D or gan iza-tion by electrophoretic deposition[J].J.Phys,Chem.B,1999,103:3818.
[14]Engelsm ann K,Lorenz W J,Schm idt E.Underpoten-tial deposition of lead on polycrystalline and single-crystal gold surface 1.Thermodynam ica[J].J.E lec-troanal.Chem.,1980,114:1.
[15〗Ren B,L i X Q,She C X.Surface Ram an spectroscopyas a versatile techn ique to study m ethanol oxidation onrough Pt electrodes[J].E lectroch im.Acta,2000,46:193.
[16〗B iswas P C,Nodasaka Y,EnyoM,et al.E lectro-oxi-dation of CO and m ethanol on graph ite-based p latinumelectrodes comb ined w ith oxide-supported u ltrafine goldpartic les[J].J.E lectroanal.Chem,1995,381:167.