研究以J420焊条焊接Q235钢,其焊缝于亚硫酸铵介质中的腐蚀行为.电化学方法和金相分析表明,Q235钢用J420焊条焊接后,焊缝的组织特点决定了它的耐蚀性低于母材.提高温度,增加亚硫酸铵浓度,均会促使焊缝的腐蚀速率加快.
The corrosion behavior of welding seam of the Q235 steel jointed by J420 electrode in ammonium sulfite solution was researched.The results of electrochemical method of welding seam and metallurgical structure analysis showed that the poor corrosion resisting property was determined by its structure after the Q235 steel was jointed by J420 electrode.The sulfite corrosion rate was accelerated by increasing the temperature and concentration of ammorium.
[1]Qu W e i-Jun(屈维均)(Reterences):.Chem ical Analy-sis of PaperM anufacturing Industry[M].Be ijing:Ch i-nese L ight Industry Press,1992.48~70.
[2]Feng La-Jun(冯拉俊).Corrosion and Protection of Pa-perM ak ing Equ ipm ent for Pu lp ing[M].Be ijing:Ch i-nese L ight Industry Press,1995.7~38.
[3]ZhaoM ai-Qun(赵麦群),Le i A-L i(雷阿利).M ateri-als Corrosion and Protection[M].Be ijing:Defence In-dustry Press,2002.46~56.
[4]Feng La-jun(冯拉俊),Le i A-li(雷阿利).Corrosionand protection of rotary spherical d igester for paperm ak-ing[J].Journal ofNorthwest Institute of L ight Industry,1997,15(4):23~27.
[5]L i Chun-m e(李春梅),Gu N ing(谷宁).Determ inationof corrosion rate in carbon steel by steady state polariza-tion m ethord[J].Hebe i Chem istry,1995,136(3):7~10.
[6]Yang De-Q ing杨德庆),Xu Jian-Y ing(徐坚颖).Anal-ysis of the film on the steel surface imm erse in neutralammon ium su lfite cook ing liquor[J].Journal of YunnanPolytechn ic Un iversit,1997,13(1):86~91.
[7]Huang En-Cai(黄恩才).Chem istry Reaction Engineer-ing[M].Be ijing:Chem istry Industry Press,1995.12~45.
[8]Lv De-L in(吕德林),L i Shuo-Zhu(李硕珠).W eld ingM etallograph ic Analysis[M].Be ijing:M echan ic Indus-try Press,1986.91~225.
[9]L i Guo-M in(李国敏),L iu L ie-W e i(刘烈伟).Corro-sion behavior of carbon steel in h igh pressure carbon d i-oxide saturated NaC l solutions contain ing hydrogen su l-fide[J].Journal of Ch inese Soc iety for Corrosion andProtection,2000,20(4):204~209.