欢迎访问《电化学(中英文)》期刊官方网站,今天是
研究论文

添加Sn组元对Ru-Ti-Ir阳极涂层的改性研究

  • 王科
展开
  • 海洋腐蚀与防护国家级重点实验室 中船重工七二五所青岛分部,海洋腐蚀与防护国家级重点实验室,中船重工七二五所青岛分部,海洋腐蚀与防护国家级重点实验室,中船重工七二五所青岛分部,山东大学材料科学与工程学院,山东大学材料科学与工程学院,,山东青岛266071,山东大学材料科学与工程学院山东济南250061,山东青岛266071,山东青岛266071,山东济南250061,山东济南250061

收稿日期: 2006-05-28

  修回日期: 2006-05-28

  网络出版日期: 2006-05-28

Investigation on Ru-Ti-Ir Anode Coatings Modified by Adding Sn Element

  • WANG Ke~
Expand
  • (1,2),HAN Yan~(l),WANG Jun-tao~(*1),ZHANG Xiao-ling~(2),SUN Yu-pu~(2)(1.State Key Laboratory for Marine Corrosion and Protection,Qingdao Branch of Luoyang Ship Material Research Institute,Qingdao 266071,Shandong,China,2.Department of Material Science and Engineering of Shandong University,Jinan 250061,Shandong,China

Received date: 2006-05-28

  Revised date: 2006-05-28

  Online published: 2006-05-28

摘要

应用热分解法制备不同Sn含量的Ru-Ti-Ir-Sn氧化物阳极涂层,SEM、EDX、XRD、析氯电位、电流效率及循环伏安和电化学阻抗谱等实验表明,Ru-Ti-Ir经添加Sn组元后,该阳极涂层表面形貌发生了很大变化,Sn组元的添加不仅有利于该阳极涂层析氯电位的降低,而且能够有效提高其电流效率.

本文引用格式

王科 . 添加Sn组元对Ru-Ti-Ir阳极涂层的改性研究[J]. 电化学, 2006 , 12(2) : 159 -164 . DOI: 10.61558/2993-074X.1715

Abstract

The anode coatings of Ru-Ti-Ir-Sn oxide with various Sn contents were prepared by thermal decomposition and characterized by the scanning electron microscopy(SEM),energy dispersive X-ray detector(EDX),X-ray diffraction(XRD),and the potential of chlorine evolution,current efficiency,cyclic voltammetry and electrochemical impedance spectroscopy(EIS).The results tests showed that there was a great change in the morphology of the coatings after adding Sn element.The addition of Sn not only reduced the potential of chlorine evolution,but also effectively improved the current efficiency of the anode coatings.

参考文献

[1]Trasatti S.E lectrocatalysis:understand ing the success ofDSA[J].E lectroch im ica Acta,2000,45:2377~2385. [2]Hou Zh iq iang(侯志强),Han Yan(韩严).Investigationon Ru-Ti-Ir-Sn oxide coated electrodes[J].Developm entand App lication ofM aterials,2002,17(1):28. [3]W ang B in(王彬),Hou Sh izhong(侯世忠),Han Yan(韩严),et al.Recent status of developm ent of m etaloxide coated anode for antifou ling by electrolyzing sea-water[J].Developm ent and App lication of M aterials,1998,13(1):42. [4]Balko E N,Nguyen P H.Irid ium tin m ixed oxide anodecoatings[J].Journal of App lied E lectrochem istry,1991,21:679. [5]M inors Ito,Yasush i Murakam i,Hayato Kaji,et al.Sur-face characterization ofRuO2-SnO2coated titan ium elec-trodes[J].J.E lectrochem.Soc.,1996,143(1):34. [6]L iu Yang,L i Zh iying,L i Jinghong.IrO2/SnO2elec-trodes:prepared by solgel process and the ir electrocata-lytic for pyrocatechol[J].Acta M aterialia,2004,52:723. [7]Yosh io Takasu,Satosh i Onoue,Koh ich i Kam eyam a,etal.Preparation of u ltrafine RuO2-IrO2-TiO2oxide parti-c les by solgel process[J].E lectroch im ica Acta,1994,39(13):1996. [8]W ang X in(王欣),Tang D ian(唐电),Zhou Jing-en(周敬恩).E ffects of SnO2on m icrostructure,morphology ofRuO2+SnO2+TiO2/Ti anode[J].The Ch inese Journalof NonferrousM etals,2002,12(5):922. [9]Cam ara O R,Trasatti S.Surface electrochem ical proper-ties of Ti/(RuO2+ZrO2)electrodes[J].E lectroch im icaActa,1996,41(3):420. [10]Trasatti S.Physical electrochem istry of ceram ic oxide[J].E lectroch im.Acta,1991,36(2):225. [11]Xu L K,Scantlebury J D.A study on the deactivationof an IrO2Ta2O5coated titan ium anode[J].CorrosionSc ience,2003,45:2735. [12]Kerner Z,Pajkossy T.On the origin of capac itance d is-persion of rough electrodes[J].E lectroch im.Acta,2000,46:207.