煅烧温度对锂离子正极材料Li[Ni_(0.475)Mn_(0.475)Co_(0.05)]O_2结构和电化学性能的影响

  • 王丽琴 ,
  • 焦丽芳 ,
  • 袁华堂
展开
  • 南开大学新能源材料化学研究所,南开大学新能源材料化学研究所,南开大学新能源材料化学研究所,南开大学新能源材料化学研究所 天津300071,天津300071,天津300071,天津300071

收稿日期: 2006-08-28

  修回日期: 2006-08-28

  网络出版日期: 2006-08-28

Calcined Temperatures Influence on Synthesis and Electrochemistry Charactarization of Li[Ni_(0.475)Mn_(0.475)Co_(0.05)]O_(2) for Li-ion Batteries

  • WANG Li-qin ,
  • JIAO Li-fang ,
  • YUAN Hua-tang~
Expand
  • (*),WANG Yong-mei(Institute of New Energy Material Chemistry,Nankai University,Tianjin 300071,China

Received date: 2006-08-28

  Revised date: 2006-08-28

  Online published: 2006-08-28

摘要

应用高温固相合成法制备L i[N i0.475Mn0.475Co0.05]O2.XRD,SEM,循环伏安及充放电容量测试表明,在800℃下煅烧合成的样品具有较高的嵌锂容量和良好的循环稳定性,如在20 mA/g和2.3~4.6 V的电压范围内,其首次放电比容量为178.8 mAh/g,循环30周后放电比容量仍能达到150.2 mAh/g,容量损失16.0%.

本文引用格式

王丽琴 , 焦丽芳 , 袁华堂 . 煅烧温度对锂离子正极材料Li[Ni_(0.475)Mn_(0.475)Co_(0.05)]O_2结构和电化学性能的影响[J]. 电化学, 2006 , 12(3) : 275 -278 . DOI: 10.61558/2993-074X.1736

Abstract

Layered Li[Ni_(0.475)Mn_(0.475)Co_(0.05)]O_(2) materials have been prepared by a solid-state pyrolysis method.Experiments of XRD,SEM,cyclic voltammetry and charge/discharge cycling were carried out.It can be learned that when calclined at 800 ℃,the sample showed the highest first discharge capacity of 178.8 mAh·g~(-1) at a current density of 20 mA/g in the voltage range 2.3~4.6 V.

参考文献

[1]HAN Jing-li(韩景立),LIU Q ing-guo(刘庆国).In-vestigation of a comp lex lith ium cobalt n ickel oxide aslith ium ion battery cathode m aterials prepared by a newc itrate sol-gel m ethod[J].E lectrochem istry(in Ch i-nese),2000,6(4):469. [2]Yao Chen,W ang G X.Synthesis and characterization ofL iCoxMnyN i1-x-yO2as a cathode m aterial for secondarylith ium batteries[J].J.Power Sources,2003,119:184. [3]K im JM,Chung H T.Role of transition m etals in lay-ered L i[N i,Co,Mn]O2under electrochem ical operation[J].E lectroch im ica Acta,2004,49:3573. [4]Tran N,Croguennec L,Jordy C.Influence of the syn-thesis route on the electrochem ical properties of L iN i0.425Mn0.425Co0.15O2[J].Solid State Ion ics,2005,176:1539. [5]Cao H,Zhang Yao.Synthesis and electrochem ical char-acteristics of layered L iN i0.6Co0.2Mn0.2O2cathode m ate-rial for lith ium ion batteries[J].Solid State Ion ics,2005,176:1207. [6]Sh in H S,Park H S.Synthesis of L i[N i0.475Co0.05Mn0.475]O2cathode m aterials via a carbonate process[J].Solid State Ion ics,2005,176:2577. [7]Cho TH,Park SM.E ffect of synthesis cond ition on thestructural and electrochem ical properties of L i[N i1/3Mn1/3Co1/3]O2prepared by carbonate co-prec ip itationm ethod[J].J.Power Sources,2005,142:306.