研究纳米金刚石水基稳定分散体系的组成及分散操作工艺.以低泡沫磺酸基阴离子表面活性剂作分散活化剂,比较了各种机械搅拌方式对体系稳定性的影响,并以复合镀铬作应用试验.测定了纳米金刚石复合镀铬的镀层沉积速率,镀层硬度,耐磨性等参数,由SEM观察镀层晶态结构图像.列举了试验结果、测试数据及复合镀铬的工艺条件,并对实验结果及机理进行了分析探讨.
张来祥
,
谢洪波
,
马学奎
,
赵国武
,
于恩成
,
王家智
. 纳米金刚石稳定水分散体系在复合电镀铬中的应用[J]. 电化学, 2007
, 13(3)
: 288
-292
.
DOI: 10.61558/2993-074X.1824
The nano diamond stable water disperse system was studied.The low-bublles sulfonic anion sufcace active agent had been choosed out for this system.The affect of different physics agitation mothed on the water separate system stablity were conpared.The nano diamond stable water separate system had been applied to the composite chromium electroplating on this tests.The depositing speed,hardnees and wearing capacity of plating layer were tested.And the metallography structure of plating layer was charasterized by SEM.The test results and reaction princeple were discussed.
[1]ZHU Yong-wei(朱永伟),WANG Bo-chun(王柏春),CHEN Li-fang(陈立舫).The application actaulity andforeground of nano diamond[J].Material LeadingNewspaper(in Chinese),2002,116(12):27-30.
[2]ZHANG wei-da(张书达).The apllication of nano dia-mond[J].Industry Diamond(in Chinese),2001,3:6-7.
[3]YU Jie(于杰),LIU Jian-ping(刘建平),ZHAO Gou-ping(赵国鹏).The preparation of the SiO2water sepa-rate system and application on electroplating[J].Plat-ing and Surface Finishing(in Chinese),2003,23(2):25-26.
[4]YANG Dong-qing(杨冬青),ZHANG Hua-tang(张华堂),TONG Xiao-hui(佟晓辉).The tribology capabil-ity on the nano diamond composite chromium electropla-ting layer[J].Metal Heating Treatment(in Chinese),2001,27(6):5-7.