应用电化学阻抗谱(EIS)研究碳钢在N-甲基二乙醇胺(MDEA)介质中的腐蚀行为.实验表明,未经预阴极活化处理的碳钢表面存在氧化膜,溶解氧促使它腐蚀速率增大,经活化处理去除氧化膜后则相反.在不含热稳定性盐(HSS)的MDEA溶液中,碳钢的腐蚀性随MDEA浓度的增加呈先上升后下降趋势;而在HSS高含量的溶液中,其腐蚀性则随MDEA浓度的增加而单调下降.在含有HSS模拟溶液中,碳钢的阳极极化EIS随极化电位由低到高分别出现感抗、负阻抗以及Warburg阻抗响应等特征,对应于孔蚀、活化状态向钝化状态过渡以及进入钝化的趋势,腐蚀反应的阴极过程表现为电化学反应和扩散传质混合控制,阳极过程为电化学反应控制.

Corrosion behavior of carbon steel in methyldiethanolamine(MDEA) solution was investigated by Electrochemical Impedance Spectroscopy(EIS).The results were showed that the corrosion rate of carbon steel in solution containing dissolved oxygen is higher than that in solution removed of dissolved oxygen before cathodic activation.They were reversed after cathodic activation.The corrosion rate is increased at first and then decreased when the concentration of MDEA is increased in the blank solutions.In the simulated solutions containing quantities of!heat-stable salts(HSS),the corrosion rate is decreased monotonously with increase of the MDEA concentration.As anodic polarization potential is increased,the EIS of carbon steel in HSS simulated solution showed characteristics of inductive shrinkage,negative impedance and Warburg-response,which implied pitting corrosion,transition from active state to passive state and passive state,respectively.The rate of cathodic reduction is determined by both electrochemical reaction and diffusion process.The rate-determining step of the anodic dissolution is electrochemical reaction.