选用合适模板剂由溶胶凝胶法合成高度有序介孔结构的磷酸钛正极材料.研究煅烧温度对材料孔结构及材料的电化学性能的影响,合成样品的结构形貌和比表面分别用XRD、BET、TEM及元素分析仪表征.充放电测试结果表明,该介孔结构正极材料表现出优越的电化学性能,以150 mA/g充放电,首次放电容量高达94 mAh/g,而不含模板剂无孔结构的材料放电容量仅37 mAh/g.
Ordered porous titanium phosphate materials were prepared by using the surfactant template combined with the sol-gel method.The samples were characterized by small angle X-ray diffraction(SA-XRD) method,N2 adsorption/desorption techniques,high resolution transmission electron microscopy(HRTEM) and element analysis.It is found that the calcination temperature is a big influence on the porous structure,and electrochemical performance of the titanium phosphate materials.,and the mesoporous titanium phosphate showed good performance in the electrochemical test,the first discharge capacity is 94 mAh/g at the current density of 150 mA/g.On the other hand,the no porous material with a low capacity of 37 mAh/g under the same charge-discharge condition.
[1]Chung S Y,Bloking J T,Chiang Y M.Electronicallyconductive phospho-olivines as lithium storage elec-trodes[J].Nature Materials,2002.1:123.
[2]SHI Zhi-cong(施志聪),LI Chen(李晨),YANG Yong(杨勇).Study on electrochemical performance of anew type cathode material of LiFePO4[J].Electro-chemistry(in Chinese),2003,9(1):9.
[3]Tarascon J M,Armand M.Issues and challenges facingrechargeable lithium batteries[J].Nature,2001,414:359.
[4]Kavan L,Kalbac M,Zukalova M,et al.Lithium storagein nanostructured TiO2made by hydrothermal growth[J].Chem Mater,2004,16:477.
[5]Gao X,Zhu H,Pan G,et al.Preparation and electro-chemical characterization of anatase nanorods for lithi-um-inserting electrode material[J].Phys Chem B,2004,108:2868.
[6]Shi Z C,Wang Q,Ye W L,et al.Synthesis and char-acterization of mesoporous titanium pyrophosphate aslithium intercalation electrode materials[J].Micro-porous and Mesoporous Materials,2006,88(1~3):232-237.
[7]Shi Z C,Li Y X,Ye W L,et al.Mesoporous FePO4with enhanced electrochemical performance as cathodematerials of rechargeable lithium batteries[J].Electro-chemical and Solid State Letters,2005,8(8):A396-A399.
[8]Huo Q,Margolese D I,Stucky G D.Surfactant controlof phases in the synthesis of mesoporous silica-basedmaterials[J].Chem Mater,1996,8:1147.
[9]Huo Q,Margolese D I,Ciesia Feng,et al.Genealizedsynthesis of periodic surface/inorganic composite mate-rials[J].Nature,1994,368(6469):317.
[10]Kresge C T,Leonowicz ME,Roth W J,et al.Orderedmesoporous molecular sieves synthesized by a liquid-crystal template mechanism[J].Nature,1992,359(6397):710.
[11]Beck J S,Vartuli J C,Roth W J,et al.A new familyof mesoporous molecular sieves prepared with liquidcrystal templates[J].J Am Chem Soc,1992,114:10834.
[12]Huo Q,Leon R,Petroff P M,et al.Mesostructure de-sign with gemini surfactants:Supercage formation in athree-dimensional hexagonal array[J].Science,1995,268(5215):1324.
[13]Yang P D,Zhao D Y,David I Margolese,et al.Gen-eralized syntheses of large-poremesoporous metal oxideswith semi-crystalline frameworks[J].Nature,1998,396(6707):152-155.
[14]XU Ru-ren(徐如人),PANG Wen-qin(庞文琴),YUJi-hong(于吉红),et al.Sieve and porous materialschemistry[M].Beijing:Science Publishing Company,2004.
[15]Sébastien Patoux,Christian Masquelier.Lithium inser-tion into titanium phosphates,silicates,and sulfates[J].Chem Mater,2002,14:5057-5068.