本文研究自组装单层保护金纳米团簇(C12Au MPC)在常温下二氯甲烷溶液中的量子化电容充电效应.示差脉冲伏安曲线显示金核平均直径为2.0 nm的C12Au MPC在-0.6~0.6 V电位区间内有9个明显的量子化电容充电峰,其双电层电容总的变化趋势为在零电荷电位附近最小,随着电位正移或负移电容变大.而且随着该金核尺寸的增大,MPC双电层电容值也变大.
Quantized capacitance charging was observed for the C12Au monolayer-protected clusters self-assembled on a gold electrode surface in CH2Cl2 solution at room temperature.The result from differential pulse voltammetry(DPV) of C12Au MPC with average core diameter of 2.0 nm showed that which appear nine entries well-defined quantized capacitance charging peaks within the potential range of-0.6 to +0.6 V.The change trend of MPC double-layer capacitances(CMPC) was that the value of CMPC was smallest near zero charge potential and increased with potential positive or negative transfer.In addition,the effect of Au core size on quantized capacitance charging of C12Au MPC was studied.The results showed that the value of CMPC increased with increasing Au core size.
[1]Taratula O,Chen A D,Zhang J M,et al.Highly a-ligned ribbon-shaped Pd nanoparticle assemblies byspontaneous organization[J].J Phys Chem C,2007,111:7666-7670.
[2]Sun S H,Zeng H,Robinson D B,et al.MonodisperseMFe2O4(M=Fe,Co,Mn)nanoparticles[J].J AmChem Soc,2004,126(1):273-279.
[3]Stevenson K A,Muralidharan G,Maya L,et al.Cova-lent attachment of gold nanoparticles to DNA templates[J].J Nanosci and Nanotech,2002,2(3~4):397-404.
[4]Schmid G,Baumle M,Geerkens M,et al.Current andfuture applications of nanoclusters[J].Chem Soc Rev,1999,28(3):179-185.
[5]Feldheim D L,Keating C D.Self-assembly of single e-lectron transistors and related devices[J].Chem SocRev,1998,27(1):1-12.
[6]Chen S,Murray R W,Feldberg S W.Quantized capac-itance charging of monolayer-protected Au clusters[J].J Phys Chem B,1998,102(49):9898-9907.
[7]Chen S,Ingram R S,Hostetler M J,et al.Gold nano-electrodes of varied size:Transition to molecule-likecharging[J].Science,1998,280:2098-2101.
[8]Ingram R S,Hostetler MJ,Murray R W,et al.28 kDaalkanethiolate-protected Au clusters give analogous solu-tion electrochemistry and STM coulomb staircases[J].J Am Chem Soc,1997,119:9279-9280.
[9]Chen S,Pei R,Zhao T,et al.Gold nanoparticle as-semblies by metal ion-pyridine complexation and theirrectified quantized charging im aqueous solutions[J].J Phys Chem B,2002,106:1903-1908.
[10]Chen S,Pei R.Ion-induced rectification of nanoparti-cle quantized capacitance charging in aqueous solutions[J].J Am Chem Soc,2001,123:10607-10615.
[11]Chen S.Nanoparticle assemblies:“Rectified”quan-tized charging in aqueous media[J].J Am ChemSoc,2000,122:7420-7421.
[12]Chen S.Self-assembling of monolayer-protected goldnanoparticles[J].J Phys Chem B,2000,104(4):663-667.
[13]Zamborini F P,Hicks J F,Murray R W.Quantizeddouble layer charging of nanoparticle films assembledusing carboxylate/(Cu2+or Zn2+)/carboxylate bridges[J].J Am Chem Soc,2000,122:4514-4515.
[14]Chen S,Murray R W.Electrochemical quantized ca-pacitance charging of surface ensembles of gold nanop-articles[J].J Phys Chem B,1999,103:9996-10000.
[15]Chen Yujing(陈玉静),Hu Xiaoya(胡效亚),WangChengyin(王頳胤),et al.Studies on quantized ca-pacitance charging of monolayer-protected clusters withmicroelectrode[J].Chem J Chinese Universities(inChinese),2003,24(10):1779-1783.
[16]Schaaff TG,Shafigullin MN,Khoury J T,et al.Iso-lation of smaller nanocrystal Au molecules:robustquantum effects in optical spectra[J].J Phys ChemB,1997,101:7885-7891.
[17]Brust M,Walker M,Bethell D,et al.Synthesis ofthiol-derivatised gold nanoparticles in a two-phase liq-uid-liquid system[J].J Chem Soc Chem Commun,1994,801-802.