Synthesis of AgV_3O_8 as High-Capacity of Cathode Materials for Lithium Secondary Batteries via a Soft Chemistry Technique

  • CAO Xiao-yu ,
  • LI Tao ,
  • XIE Ling-ling ,
  • YAN Xiang-yang ,
  • WANG Chi-wei
Expand
  • (1.School of Chemistry and Chemical Engineering,Henan University of Technology,Zhengzhou 450001,China;2.Shenzhen Bak Battery Co.,LTD,Shenzhen 518119,Guangdong,China

Received date: 2008-05-28

  Revised date: 2008-05-28

  Online published: 2008-05-28

摘要

应用软化学方法合成层状AgV3O8正极材料,并用XRD(粉末X-射线衍射)、SEM(扫描电子显微镜)和LPSA(激光粒度分析)表征了材料的结构和形貌,采用恒流充放电技术研究了其电化学性能.SEM和LPSA测试结果显示所制备的材料具有较小的颗粒尺寸和较窄的粒度分布区间.恒流充放电测试结果表明,该材料具有高的放电比容量,其中400℃下获得的材料首次放电容量高达760.5 mAh/g.

本文引用格式

曹晓雨 , 李涛 , 谢玲玲 , 闫向阳 , 王驰伟 . 软化学技术合成高容量锂二次电池正极材料AgV_3O_8(英文)[J]. 电化学, 2008 , 14(2) : 184 -189 . DOI: 10.61558/2993-074X.1888

Abstract

The layered cathode material of AgV3O8 has been prepared for the lithium secondary batteries via the soft chemistry technique. The so-synthesized powders were characterized by XRD(powder X-ray diffraction),SEM(scanning electron microscope) and LPSA(laser particle size analysis).The electrochemical property was investigated by the galvanostatic discharge-charge technique.The results indicated that the particale sizes of AgV3O8 prepared were small in the distribution of narrow range,which leads to high discharge capacity.Among them,the material synthesized at 400 ℃ displayed the first discharge capacity of 760.5 mAh/g.

参考文献

[1]Whittingham MS.Lithium batteries and cathode materi-als[J].Chem Rev,2004,104:4271-4301. [2]Tarascon J M,Armand M.Issues and challenges facingrechargeable lithium batteries[J].Nature,2001,414:359-367. [3]Cao X Y,Xie J G,Zhan H,et al.Low-temperaturesynthesis of Cu2V6O17from V2O5gel[J].J New MatElectrochem Sys,2006,9:47-50. [4]Cao X Y,Zhan H,Xie J G,et al.Synthesis ofAg2V4O11as a cathode material for lithium battery via arheological phase method[J].Mater Lett,2006,60:435-438. [5]Xie J G,Li J X,Zhan H,et al.Low temperature sol-gel synthesis of Li1.2V3O8from V2O5gel[J].MaterLett,2003,57:2680-2687. [6]Xie J G,Cao X Y,Li J X,et al.Ultrasonic sol-gelsynthesis of silver vanadium oxides from V2O5gel[J].Ultrason Sonochem,2005,12:289-293. [7]Takeuchi K J,Marschilok A C,Davis S M,et al.Silvevanadium oxides and related battery applications[J].Coordin Chem Rev,2001,(219-221):283-310. [8]Kawakita J,Katayama Y,Miura T,et al.Lithium in-sertion behaviour of silver vanadium bronze[J].SolidState Ionics,1997,99:71-78. [9]Cho J,Park B.Preparation and electrochemical/ther-mal properties of LiNi0.74Co0.26O2cathode material[J].J Power Sources,2001,92,35-39. [10]Liu E H(刘恩辉),Li X H(李新海),He Z Q(何则强),et al.Synthesis and electrochemical character-ization of LiV3O8[J].Battery Bimonthly(in Chi-nese),2004,34:164-165. [11]Liang H G,Qiu X P,Chen H L,et al.Analysis ofhigh rate performance of nanoparticled lithium cobaltoxides prepared in molten KNO3for rechargeable lithi-um-ion batteries[J].Electrochem Commun,2004,6:789-794.