应用化学镀方法,以活化-敏化处理的活性炭作载体,制备高分散催化剂PtRu/C和PtRuSn/C.XRD、TEM及电化学测试表明,该催化剂Pt、Ru、Sn形成合金.金属颗粒的平均粒径约为3 nm.PtRu/C和PtRuSn/C二者对乙醇的阳极氧化都具有良好的催化活性和稳定性.
朱静
,
苏怡
,
马华
,
程方益
,
陶占良
,
梁静
,
陈军
. 化学镀制备高性能直接乙醇燃料电池(DEFC)阳极催化剂PtRu/C和PtRuSn/C[J]. 电化学, 2008
, 14(2)
: 150
-154
.
DOI: 10.61558/2993-074X.1881
In this paper,the preparation,characterization,and ethanol electrocatalytic oxidation of Pt0.5Ru0.5/C and Pt0.5Ru0.15Sn0.35/C electrocatalysts were reported.The electroless-deposition with sensitization-activation pretreatment was applied to prepare Pt0.5Ru0.5/C and Pt0.5Ru0.15Sn0.35/C electrocatalysts. The XRD and TEM analyses showed that the as-prepared catalysts were composed of well-dispersed PtRu or PtRuSn nanoparticles with an average particle size of about 3 nm.The electrochemical measurements demonstrated that the as-prepared Pt0.5Ru0.5/C and Pt0.5Ru0.15Sn0.35/C catalysts exhibited much enhanced peak current density for ethanol electrooxidation as compared to that synthesized without pretreatment.This result revealed that the pretreatment is favorable to the dispersion,size distribution and alloy degree of the nanocatalysts on the carbon support.In particular,the peak current density of ethanol oxidation on Pt0.5Ru0.15Sn0.35/C was nearly twice larger than that of Pt0.5Ru0.5/C,indicating their potential application in DEFC with a synergic effect of Ru and Sn.
[1]Song Shuqin(宋树芹),Wang Yi(王毅),Shen Pei-kang(沈培康).Thermodynamic and kinetic considera-tions for ethanol electrooxidation in direct ethanol fuelcells[J].Chinese Journal of Catalysis,2007,28(9):752-754.
[2]Song Shuqing(宋树芹),Chen Likang(陈利康),LiuJianguo(刘建国),et al.Preliminary study on directethanol fuel cell[J].Electrochemistry(in Chinese),2002,8(1):105-110.
[3]Xue Xinzhong,Lu Tianhong,Liu Changpeng,et al.Novel preparation method of Pt-Ru/C catalyst using imi-dazolium ionic liquid as solvent[J].Electrochim Acta,2005,50(16-17):3470-3478.
[4]Wei Zhaobin(魏昭彬),Liu Jianguo(刘建国),QiaoYaguang(乔亚光),et al.Performance of a directmethanol fuel cell[J].Electrochemistry(in Chinese),2001,7(2):228-233.
[5]Li Huanqiao,Sun Gongquan,Cao Lei,et al.Compari-son of different promotion effect of PtRu/C and PtRuSn/C electrocatalysts for ethanol electro-oxidation[J].Electrochim Acta,2007,52:6622-6629.
[6]Bai Yuxia,Li Jinfeng,Qiu Xinping,et al.Mesocarbonmicrobeads supported PtSn catalysts for electrochemicaloxidation of ethanol[J].J Mater Sci,2007,42:4508-4512.
[7]Colmati F,Antolini E,Gonalez E R.Ethanol oxidationon carbon supported Pt-Sn electrocatalysts prepared byreduction with formic acid[J].J Electrochem Soc,2007,154(1):B39-B47.
[8]Zhou Weijiang,Song Shuqing,Li Wenzhen,et al.Pt-based anode catalysts for direct ethanol fuel cells[J].Solid State Ionics,2004,175:797-803.
[9]Zhu Jing,Su Yi,Cheng Fangyi,et al.Improving theperformance of PtRu/C catalysts for methanol oxidationby sensitization and activation treatment[J].J PowerSources,2007,166:331-336.
[10]Guo J W,Zhao T S,Prabhuram J,et al.Preparationand characterization of a PtRu/C nanocatalyst for directmethanol fuel cells[J].Electrochim Acta,2005,51:754-763.
[11]Neto A O,Dias R R,Tusi MM,et al.Electro-oxida-tion of methanol and ethanol using PtRu/C,PtSn/Cand PtSnRu/C electrocatalysts prepared by an alcohol-reduction process[J].J Power Sources,2007,166:87-91.
[12]Lu Qingye,Yang Bo,Zhuang Lin,et al.Pattern rec-ognition on the structure-activity relationship of nanoPt-Ru catalysts:methodology and preliminary demon-stration[J].J Phys Chem B,2005,109:8873-8879.
[13]Colmati F,Antolini E,Gonzalez E R.Effect of tem-perature on the mechanism of ethanol oxidation on car-bon supported Pt,PtRu and Pt3Sn electrocatalysts[J].J Power Sources,2006,157:98-103.
[14]Suffredini HB,Tricoli V,Vatistas N,et al.Electro-oxidation of methanol and ethanol using a Pt-RuO2/Ccomposite prepared by the sol-gel technique and sup-ported on boron-doped diamond[J].J Power Sources,2006,158:124-128.