应用电化学阳极氧化法,以Fe(NO3)3-HF的混合水溶液作电解液在Ti基底上制备Fe掺杂TiO2纳米管阵列.FESEM、Raman、XPS、DRS等测试表明:经Fe掺杂的TiO2纳米管阵列,管径50~90 nm,管长约200nm.与未掺杂TiO2纳米管阵列相比,前者的紫外可见起始吸收带边随着Fe掺入量的增加而红移;而光电化学性质如光电流也随之显著提高.
李静
,
孙岚
,
庄惠芳
,
王成林
,
杜荣归
,
林昌健
. 铁掺杂TiO_2纳米管阵列制备及其光电化学性质[J]. 电化学, 2008
, 14(2)
: 213
-217
.
DOI: 10.61558/2993-074X.1894
The Fe-doped TiO2 nanotube arrays were fabricated in Fe(NO3)3-HF mixing solutions by electrochemical anodic oxidation method,and characterized by FESEM,Raman,XPS and DRS.The effect of Fe concentratiions on photoelectrochemical property of the arrays was also investigated.The diameters and lengths of Fe-doped TiO2 nanotube arrays were 50~90 nm and about 200 nm,respectively.Compared with the undoped TiO2 nanotube arrays,the absorption edge of Fe-doped TiO2 nanotube arrays appeared red shifting.The more Fe content,the larger red shifting,in addition,the photocurrent of Fe-doped TiO2 nanotube arrays increased obviously.
[1]Gong D,Grimes C A,Varghese O K,et al.Titaniumoxide nanotube arrays prepared by anodic oxidation[J].J Mater Res,2001,16(12):3331-3334.
[2]Fujishima A,Rao T N,Tryk D A.Titanium dixxidephotocatalysis[J].J Photochem Photobiol C-Photo-chem Rev,2000,1(1):1-21.
[3]Mor G K,Carvalho M A,Varghese O K,et al.Aroom-temperature TiO2-naotube hydrogen sensor able toselfclean photoactively from environmental contamina-tion[J].J Mater Res,2004,19(2):628-634.
[4]Fujishima A,Honda K.Electrochemical photolysis ofwater at a semiconductor electrode[J].Nature,1972,238:37-41.
[5]Gratzel M.Dye-sensitisized solar cells[J].J Photo-chem Photobiol C-Photochem Rev,2003,4(2):145-153.
[6]Yang B C,Uchida M,Kim H-M,et al.Preparation ofbioactive titanium metal via anodic oxidation treatment[J].Biomaterials,2004,25(6):1003-1010.
[7]Ad偄n C,Bahamonde A,Fern偄ndez-Garc姫a M,et al.Stucture and activity of nanonized iron-doped anataseTiO2catalysts for phenol photocatalytic degradation[J].Applied Catalysis B:Environmental,2007,72:11-17.
[8]Xin B F,Ren Z Y,Fu HG,et al.Study on the mech-anisms of photoinduced carriers separation and recombi-nation for Fe3+-TiO2photocatalysts[J].Applied Su-face Science,2007,253:4390-4395.
[9]Cao Jiang-lin(曹江林),Wu Zu-cheng(吴祖成),Zhang Jian-qing(张鉴清),et al.Cathodic Co-electro-deposition of Fe3+-doped TiO2thin films and their pho-tocatalytic activity under visible light[J].Journal ofInorganic Materials(in Chinese),2007,22:514-518.
[10]LAI Yue-ku(赖跃坤),SUN Lan(孙岚),LIN Chang-jian(林昌健),et al.Electrochemical fabrication andformation mechanism of TiO2nanotube arrays on metal-lic titanium surface[J].Acta Phisico-Chimica Sinica(in Chinese),2004,20(9):1063-1066.
[11]Ohsaka T,Yamaoka S,Shimomura O.Effect of hudro-static pressur on the Raman spectrum of anatase(TiO2)[J].Solid State Commun,1979,30:345-347.
[12]XIAO Mei-qun(肖美群),SHEN Jia-nian(沈嘉年),LI Mou-cheng(李谋成),et al.Effect of Fe~(3+)dopant on absorption spectra and photo catalysis activi-ty of titanium dioxide film[J].Shanghai Metals(inChinese),2004,26(4):13-16.