使用去合金法制备了孔径和孔壁均匀的纳米多孔金(NPG)电极.研究发现NPG对甲酸、甲醛的氧化具有很高的电催化活性.如在NPG基体再沉积微量的铂,不仅明显改善了NPG的结构稳定性,而且由于Pt、Au两组分之间的协同效应而使该催化剂对有机小分子的电催化氧化具有比纯铂更高的催化活性和更强的抗催化毒物能力.
The nanoporous gold(NPG) electrodes with uniform pore sizes and ligaments were prepared by using a simple dealloying method.The as-prepared NPG showed high catalytic activity towards the oxidation of formic acid and formaldehyde.After tiny amount of platinum was deposited onto the NPG substrate,not only the structure stability of NPG was greatly improved,but also the Pt-Au bimetallic catalysts displayed the better catalytic activity and the stronger poison resistance towards the electrooxidation of small organic molecules than the bulk platinum due to synergistic effect between Au and Pt compositions.
[1]Rosler J,Mukherji D.Design of nanoporous superalloymembranes for functional applications[J].Adv EngMater,2003,5:916-918.
[2]Kong J,Franklin NR,Zhou C W,et al.Nanotube mo-lecular wires as chemical sensors[J].Science,2000,287:622-625.
[3]Jia F L,Yu C,Deng K,et al.Nanoporous metal(Cu,Ag,Au)films with high surface area:general fabrica-tion and preliminary electrochemical performance[J].JPhys Chem C,2007,111:8424-8431.
[4]Kramer D,Viswanath R N,Weissmuller J.Surface-stress induced macroscopic bending of nanoporous goldcantilevers[J].Nano Lett,2004,4:793-796.
[5]Liu J,Feng X,Fryxell G E,et al.Hybrid mesoporousmaterials with functionalized monolayers[J].Adv Ma-ter,1998,10:161-165.
[6]DingY,ErlebacherJ.Nanoporousmetalswithcontrolledmultimodal pore size distribution[J].J Am Chem Soc,2003,125:7772-7773.
[7]Ding Y,Kim Y J,Erlebacher J.Nanoporous gold leaf:“Ancient technology”/advanced material[J].AdvMater,2004,16:1897-1900.
[8]Xu C X,Su J X,Xu X H,et al.Low temperature COoxidation over unsupported nanoporous gold[J].J AmChem Soc,2007,129:42-43.
[9]Zhang J T,Liu P P,Ma H Y,et al.Nanostructuredporous gold for methanol electro-oxidation[J].J PhysChem C,2007,111:10382-10388.
[10]Nagahara Y,Hara M,Yoshimoto S,et al.In situscanning tunneling microscopy examination of molecu-lar adlayers of haloplatinate complexes and electro-chemically produced platinum nanoparticles on Au(111)[J].J Phys Chem B,2004,108:3224-3230.
[11]Trasatti S,Petrii O A.Real surface area measurementsin electrochemistry[J].Pure Appl Chem,1991,63:711-734.
[12]Silva F,Martins A.Surface reconstruction of gold sin-gle crystals:electrochemical evidence of the effect ofadsorbed anions and influence of step and terraces[J].Electrochim Acta,1998,44:919-929.
[13]Xiang J,Wu B L,Chen S L.Investigation of themechanism of the electrochemical oxidation of formicacid at a gold electrode in sulfuric acid solution[J].J Electroanal.Chem,2001,517:95-100.
[14]Park I S,Lee K S,Choi J H,et al.Surface structureof Pt-modified Au nanoparticles and electrocatalyticactivity in formic acid electro-oxidation[J].J PhysChem C,2007,111:19126-19133.
[15]Zhou W J,Lee J Y.Highly active core?shell Au@Pd catalyst for formic acid electrooxidation[J].Elec-trochem Commun,2007,9:1725-1729.
[16]Wang X,Tang Y W,Gao Y,et al.Carbon-supportedPd-Ir catalyst as anodic catalyst in direct formic acidfuel cell[J].J Power Sources,2008,175:784-788.
[17]Karantonis A,Koutsaftis D,Kouloumbi N.Bistability,oscillations and bifurcations of the electrocatalytic oxi-dation of HCHO on Pt[J].Chem Phys Lett,2006,422:78-82.