应用电位扫描法制备3种铂与氢钨青铜(HxWO3)的复合电极,即铂上沉积氢钨青铜(HxWO3/Pt),氢钨青铜上沉积铂(Pt/HxWO3)及铂和氢钨青铜共沉积(Pt-HxWO3).测试结果表明,氢钨青铜能显著提高铂电催化对氧还原的活性,其中以复合电极Pt/HxWO3的电催化活性最高,这可能是因为在玻碳基底上先电沉积氢钨青铜再电沉积铂增加了铂的有效比表面,该电极制备为减少铂用量提供一条有效途径.
关键词：
氧还原; 催化; 氢钨青铜; 铂; 复合
郭盼盼
,
黄幼菊
,
杨红艳
,
李伟
,
张庆龙
,
李伟善
. Pt-H_xWO_3复合电极的制备及其对氧还原的电催化[J]. 电化学, 2008
, 14(4)
: 398
-401
.
DOI: 10.61558/2993-074X.1929
Three composite electrodes of platinum with hydrogen tungsten bronze(HxWO3)were prepared by voltammetry: hydrogen tungsten bronze deposited on platinum(HxWO3/Pt);platinum deposited on hydrogen tungsten bronze(Pt/HxWO3) and codeposited platinum and hydrogen tungsten bronze(Pt-HxWO3).The eletro-catalytic activities of three electrodes toward oxygen reduction reaction were studied.It is found that the catalytic activity of platinum can be improved by introducing with hydrogen tungsten bronze.Among these composite electrodes Pt/HxWO3,and the electrode shows the best eletro-catalytic activity toward oxygen reduction reaction,hence,provides a new way for reducing loading of noble metal in the application for fuel cell.
[1]Huang Y J,Li W S,Huang QD,et al.Catalytic activ-ity improvement of platinum toward oxygen reduction re-action promoted by hydrogen molybdenum bronze[J].Chem J Chinese Universities,2007,28(5):918-921.
[2]Li W S,Tian L P,Huang Q M,et al.Catalytic oxida-tion of methanol on molybdate-modified platinum elec-trode in sulfuric acid solution[J].Journal of PowerSources,2002,104:281-288.
[3]Khyzhun Yu O,Solonin Yu M,Dobrovolsky VD.Elec-tronic structure of hexagonal tungsten trioxide:XPS,XES,and XAS studies[J].Journal of Alloys and Com-pounds,2001,320:1-6.
[4]Paluselli D,Marsen B,Miller E L,et al.Nitrogen do-ping of reactively sputtered tungsten oxide films[J].Electrochemical and Solid-State Letters,2005,8(11):G301-G303.
[5]Eda K,Sukejima A,Sotani N.A new synthetic routefor mixed-valence compounds:leaching treatments ofhydrogen molybdenum bronze[J].Journal of SolidState Chemistry,2001,159:51-58.
[6]Lu J,Du J H,Li W S,et al.Formation and oxidationof hydrogen molybdenum bronze on platinum electrodein sulfuric acid solution[J].Chinese Chemical Letters,2004,15:703-708.
[7]Du J H(都君华),Xu X H(许雪惠),Li H(李红),et al.Electrocatalytic oxidation of formic acid on molyb-date-modified platinum electrode[J].Electrochemis-try,2002,8(4):420-426.
[8]Miller E L,Marsen B,Cole B,et al.Low-temperaturereactively sputtered tungsten oxide films for solar-pow-ered water splitting applications[J].Electrochimicaland Solid-state Letters,2006,9(7):G248-G250.
[9]Deepa M,Joshi A G,Srivastava A K,et al.Agnihotryelectrochromic nanostructured tungsten oxide films bySol-gel:structure and intercalation properties[J].JElectrochem Soc,2006,153(5):C365-C367.
[10]Scarminio J,Moraes Mab de,Dias Rce,et al.Tung-sten oxide films of high electrochromic efficiencies ob-tained by deposition[J].Electrochemical and Solid-State Letters,2003,6(6):H9-H12.
[11]Hersh HN,Kramer W E,McGee J H.Mechanism ofelectrochromism in WO3[J].Applied Physics Letters,1975,27(12):646.
[12]Huo L H,Zhao H,M Fabrice,et al.Synthesis andmixed conductivity of ammonium tungsten bronze withtunneling structures[J].Solid State Sciences,2004(6):679-688.
[13]Filho AGS,Matias JGN,Dias N L,et al.Microstruc-tural and electrical properties of sintered tungsten triox-ide[J].Journal of Materials Science,1999,5(34):1031-1035.