本文应用一步阳极氧化法在铝表面制作纳米粗糙结构的超亲水表面.考察控槽压、控电流及氧化时间对氧化铝表面超亲水性的影响.测试表明,控电流法更有利于制作超亲水表面,增大电流密度可缩短氧化时间,该法可制作稳定性好、机械强度高的超亲水氧化铝表面,富有潜在的应用价值.
Hydrophilic aluminum oxide is popularly used for heat exchanger of air-condition.Herein,we developed a simple method to prepare superhydrophilic aluminum oxide on the surface of aluminum through single-step electrochemical oxidization.The morphologies and water contact angles on surfaces of alumina fabricated under different electrochemical conditions were investgated.Superhydrophilic surfaces fabricated by this method have good stability and high mechanical strength with water contact angle almost 0°.Coated with low surface energy materials,superhydrophilc alumina will be converted to superhydrophobic.
[1]Gan W P(甘卫平),Ji D Y(吉冬英),Pang X(庞欣).Composite hydrophilic coating for conditioner alu-minum Fins[J].Transactions of Nonferrous Metals So-ciety of China(in Chinese),1999,9(3):510-513.
[2]Kwangtaek H,Webb R L.Wetting coatings for dehu-midifying heat exchangers[J].Hvac&R Res,2000.6(3):229-242.
[3]Pizarro G D C,Marambio O G,Jeria-Orell M,et al.Preparation,characterization,and thermal properties ofhydrophilic copolymers:p-Chlorophenylmaleimides withhydroxylethyl methacrylate and beta-methyl itaconate[J].Polym Int,2007,56(9):1166-1172.
[4]Julie B,Ian H,Brendan J H.Preparation,character-ization,and thermal properties of controllable metal?imidazole complex curing agents for epoxy resins[J].JAppl Polym Sci,2000,75:201-217.
[5]Kaoru T,Takamasa Y,Tomohiro O.Super oil-repellentsurfaces[J].Angew Chem,1997,36:1011-1012.
[6]Shibuichi S,Yamamoto T,Onda T,et al.Super water-and oil-repellent surfaces resulting from fractal structure[J].J Colloid Interface Sci,1998,208(1):287-294.
[7]Masuda H,Fukuda K.Ordered metal nanohole arraysmade by a two-step replication of honeycomb structuresof anodic alumina[J].Science,1995,268(5216):1466-1468.
[8]Masuda H,Asoh H,Watanabe M,et al.Square andtriangular nanohole array architectures in anodic alumina[J].Adv Mater,2001,13(3):189-192.
[9]Xiang J(向娟),Tian J H(田景华),Ni Z M(倪子绵),et al.Template synthesis of highly ordered mono-crystalline metal nanowire arrays by a two-step AC elec-trodeposition[J].J Electrochemistry(in Chinese),2004,10(1):9-12.