采用O2氧化法在碱性条件下氧化Mn2+,制备Li-birnessite型层状MnO2.X射线衍射、扫描电子显微镜、BET、热重等技术表征MnO2样品的性能.以放充电法测试Li-birnessite正极材料性能.结果表明,Li-birnessite结晶良好,层间距约为0.70 nm,呈球状或类球状.以Li-birnessite为正极材料的扣式电池在0.2 C(40 mA/g)条件下放电时容量高达203 mAh/g,且具有良好的倍率性能.
黄行康
,
常海涛
,
甘健龙
,
张清顺
,
岳红军
,
吕东平
. Li-birnessite型层状二氧化锰的合成及电化学性能[J]. 电化学, 2009
, 15(2)
: 194
-197
.
DOI: 10.61558/2993-074X.1978
Layered Li-birnessite was prepared by means of oxidizing Mn2+ with O2 gas in alkaline media.The as-prepared sample was characterized by scanning electron microscopy(SEM),X-ray diffraction(XRD),BET and thermogravimetric/diffenential thermal analysis(TG/DTA) techniques.The electrochemical properties of the material were also investigated.The results show that such a Li-birnessite consists of well-crystallized spherical particles with an interlayer distance of 0.70 nm.The Li-birnessite delivered a high discharge capacity of 203 mAh/g at a rate of 0.2 C(40 mA/g),and had good rate capability as well.
[1]Thackeray M M.Manganese oxides for lithium batteries[J].Prog Solid State Chem,1997,25(1/2):1-71.
[2]GAO Jun(高军),HUANG Xing-kang(黄行康),YANG Yong(杨勇).Electrochemical capacitancecharacteristics for MnO2/C composite[J].Electro-chemistry(in Chinese),2007,13(3):279-283.
[3]ZHAO Feng-ming(赵峰鸣),MAChun-an(马淳安),CHU You-qun(褚有群),et al.Oxygen reduction onNi-MnO2electrode in alkaline solution[J].Acta Phy-Chim Sin(in Chinese),2006,22(6):716-720.
[4]ZHAO Li-li(赵丽丽),WANG Rong-shu(王榕树).Preparation of MnO2(Li)and its ion exchange kinetics[J].Acta Phy-Chim Sin(in Chinese),2003,19(10):933-937.
[5]Li W N,Yuan J K,Gomez-Mower S,et al.Synthesisof single crystal manganese oxide octahedral molecularsieve(OMS)nanostructures with tunable tunnels andshapes[J].J Phys Chem B,2006,110:3066-3070.
[6]Gaillot A C,Lanson B,Drits V A.Structure of birnes-site obtained from decomposition of permanganate undersoft hydrothermal conditions.I.Chemical and structuralevolution as a function of temperature[J].Chem Ma-ter,2005,17,(11):2959-2975.
[7]Morales J,Sanchez L,Bach S,et al.Synthesis ofLixMnOy.nH2O birnessite oxide by the hydrothermalmethod[J].Mater Lett,2002,56(5):653-659.
[8]Chitrakar R,Kanoh H,Kim Y S,et al.Synthesis oflayered-type hydrous manganese oxides from monoclinic-type LiMnO2[J].J Solid State Chem,2001,160(1):69-76.
[9]Vitins G,West K.Lithium intercalation into layeredLiMnO2[J].J Electrochem Soc,1997,144(8):2587-2592.
[10]Bach S,Pereira-Ramos J P,Baffier N.Investigation ofelectrochemical lithium insertion in lamellar ternary ox-ides of the MxMnOy.zH2O group[J].J PowerSources,1997,68(2):586-589.
[11]Leroux F,Nazar L F.3-volt manganese dioxide:theamorphous alternative[J].Solid State Ionics,1997,100(1/2):103-113.