应用交流阻抗和极化曲线测试3-氨基-1,2,4-三氮唑(ATA)和钨酸钠复合缓蚀剂对黄铜在3%NaCl溶液中的缓蚀作用.结果表明,ATA对黄铜有缓蚀作用,并以7.5 mg.L-1ATA的缓蚀效果最好,缓蚀率为87.46%,以7.5 mg.L-1ATA和0.15 mg.L-1Na2WO4配成复合缓蚀剂则对黄铜具有很好缓蚀协同效应,缓蚀效率达91.82%,属阴极型缓蚀剂.
徐群杰
,
李春香
,
倪钰宏
,
周国定
. 3-氨基-1,2,4-三氮唑和Na_2WO_4复合缓蚀剂对黄铜的缓蚀协同作用[J]. 电化学, 2009
, 15(2)
: 190
-193
.
DOI: 10.61558/2993-074X.1977
AC impedance and polarization methods were used to study the inhibition effect of ATA and the complex of ATA and Na2WO4 for brass corrosion in 3% NaCl solution.The results indicated that ATA had inhibition effect for brass corrosion.ATA showed the best inhibition effect for brass corrosion at the ATA concentration of 7.5 mg·L-1,and the inhibition efficiency was 87.46%.At the ATA concentration of 7.5 mg·L-1 and at the Na2WO4 concentration of 0.15 mg·L-1,the complex showed optimum inhibition effect for brass corrosion,and also showed synergistic effect and the inhibition efficiency reached 91.82%.The complex of ATA and Na2WO4 was cathodic corrosion inhibitor.
[1]Raichandran R,Rajendran N.Influence of benzotriazolederivatives on the dezincification of 65-35 brass in sodi-um chloride[J].Applied Surface Science,2005,239:182.
[2]Elmorsi M A,Hassanein A M.Corrosion inhibition ofcopper by heterocyclic compounds[J].Corrosion Sci-ence,1999,41:2337.
[3]Bellakhal N,Dachraoui M.Study of the benzotriazoleefficiency as a corrosion inhibitor for copper in humid airplasma[J].Materials Chemistry and Physics,2004,85:366.
[4]Lalitha A,Ramesh S,Rajeswari S.Surface protectionof copper in acid medium by azoles and surfactants[J].Electrochimica Acta,2005,51:4.
[5]El-Sayed MSherif,Erasmus R M,Comins J D.Effectsof 3-amino-1,2,4-triazole on the inhibition of coppercorrosion in acidic chloride solutions[J].Colloid andInterface Science,2007,311:144.
[6]XU Qun-jie(徐群杰),LI Chun-xiang(李春香),ZHOU Guo-ding(周国定),et al.Copper Corrosion In-hibition and Adsorption Behavior of3-Amino-1,2,4-tria-zole[J].Acta Physical Chimica-Sinica(in Chinese),2009,25(1):86.
[7]LI Yan(李燕),ZHANG Guan-yong(张关永),LU Zhu(陆柱).Application of surface analysis technology instudy on corrosion inhibition mechanism of tungstate[J].Corrosion and Protection(in Chinese),2000,21(10):447.