应用电偶电流测试法研究在中温固态NaCl盐膜-水蒸气协同作用下,纯铁的腐蚀电化学反应机理.交流阻抗(EIS)法和SEM测试表明,阻抗谱能有效地表征材料表面氧化膜的存在以及反应过程氧化物的变化趋势,其中金属的氧化层电阻与腐蚀速率之间有较好的对应关系.
The existence of electrochemical reaction during the corrosion process of pure Fe under a deposit of solid NaCl in water vapor at above 400 ℃ had been detected by measuring the corrosion current using double-layer electrode.In EIS measurement,only one capacitive loop was obtained on the pure metals and this gave the information of oxide layer on them.The electrochemical impedance spectroscopy(EIS) and scanning-electron microscopy(SEM) results testified that there is a good relationship between the resistance of oxide layer Rox and the corresion reaction rate for pure metals with different oxidation times.The electrochemical technique is an effective method for studying corrosion performance at high temperature.
[1]Wang F,Geng S,Zhu S.Corrosion behavior of a sput-tered K38G nanocrystalline coating with a solid NaCl de-posit in wet oxygen at 600 to 700℃[J].Oxid Met,2002,58:185.
[2]Wang F,Shu Y.Influence of Cr content on the corro-sion of Fe-Cr alloys:the synergistic effect of NaCl andwater vapor[J].Oxid Met,2003,59:201.
[3]Wang C,Jiang F,Wang F.Corrosion inhibition of 304stainless steel by nano-sized Ti/Si coatings in an envi-ronment containing NaCl and water vapor at 400-600℃[J].Oxid Met,2004,62:1.
[4]Shu Y,Wang F,Wu W.Corrosion behavior of pure Crwith a solid NaCl deposit in O2plus water vapor[J].Ox-id Met,2000,54:457.
[5]Shu Yong-hua.NaCl与水蒸气作用下几种材料及涂层的中温腐蚀[D].Shenyang:Institute of Metal Re-search,Chinese Academy of Sciences,1999.
[6]Li Mou-cheng.质子交换膜燃料电池金属双极板材料的腐蚀行为研究,[D].Shenyang:Institute of MetalResearch,Chinese Academy of Sciences,2002.
[7]ijerholm J,Pan J,J nsson B.Influence of grain-sizeon ionic conductivity of pure and dense alpha-Al2O3inthe temperature range 400-1000 degrees C[J].MaterSci Forum,2004,461:865.
[8]Pan J,Leygraf C,Pettersson R F AJ,et al.Character-ization of high-temperature oxide films on stainless steelsby electrochemical impedance sqectroscopy[J].OxidMet,1998,50(5/6):431.