建立实验室模拟大气腐蚀的干湿循环加速腐蚀方法.提出低碳钢锈蚀的分段演化规律,演化规律对应于锈层致密度转折和锈层结晶组分的形成,显示分段规律的合理性.实验室获得的低碳钢锈蚀演化规律与其在万宁和沈阳两个大气站现场曝晒的最新结果有相关性,证明加速腐蚀方法的可靠性.
It has been set up an accelerated method of simulating to atmospheric corrosion by using wet/dry alternate test.The rust evolution rule of mass change vs time(in logarithmic coordinate) of low carbon steel under this test shows two linear sections with different slopes,in which the rust evolution transition in weight change corresponds to the compactness transition and crystallization transition during the rust layer growth.It has found that the rust evolution rule of low carbon steel in Wanning exposure site correlates to the rust evolution rule obtained by simulating the coastal atmospheric corrosion test,and the rust evolution rule of low carbon steel in Shenyang exposure site correlates to the rust evolution rule obtained by simulating the industrial acidic rain atmospheric corrosion test.These results proved the reliability of the simulated atmospheric corrosion accelerated test.
[1]American Society for Testing and Materials:G 85-1998,Standard Practice for Modified Salt Spray(Fog)Testing G 85-94,Practice for Modified Salt Spray(Fog)Testing
[2]American Society for Testing and Materials.StandardPractice for Conducting Moist SO2Tests[S].G87-1997.
[3]The Industry Standard of Railway Ministry of China.Cy-clic Wet/Dry Corrosion Test of Weathering Steel Usingfor Railway[S].TB/T2375-1993.
[4]JIS Steel Standards:G3125,Superior atmospheric cor-rosion resisting rolled steels;G3114,Hot-rolled atmos-pheric corrosion resisting steels for welded structure[S].
[5]Nishimura H Katayama,Noda K,Kodama T.Electro-chemical behavior of rust formed on carbon steel in awet/dry environment containing chloride ions[J].Cor-rosion,2000,56:935-941
[6]Liang Caifeng(梁彩凤),Hou Wentai(候文泰),Six-teen-year atmospheric corrsion exposure study of steels[J].Journal of Chinese Society for Corrosion and Pro-tection(in Chinese),2005,25(1):1-6.
[7]Liang Caifeng(梁彩凤),Hou Wentai(候文泰).Predic-tion of atmospheric corrosion for steels[J].Journal ofChinese Society for Corrosion and Protection(in Chi-nese),2006,26(3)129-135.
[8]Hou Wentai,Liang Caifeng.Atmospheric corrosion pre-diction of steels[J].Corrosion,2004,60(3):313-322.
[9]Dong Jie(董杰),Dong Junhua(董俊华),Han Enhou(韩恩厚),et al.Corrosion behavior of rusted mildsteel under wet/dry alternate conditions[J].CorrosionScience and Protection Technology(in Chinese),2006,18(6):414.
[10]Dong Jie(董杰),Dong Junhua(董俊华),Han Enhou(韩恩厚),et al.Rusting evolvement of mild steel un-der wet/dry cycle conditon with pH4 NaHSO3solution[J].Corrosion Science and Protrction Technology(inChinese),2009,21(1):1-4.
[11]Junhua DONG,Enhou HAN,Wei KE,An introduc-tion of atmospheric corrosion research of China[J].Science and Technology of Advanced Materials,2007,8:559-565.
[12]S.Music',S.Krehula,S.Popovic',Thermal decompo-sition ofα-FeOOH[J].Materials Letter,2004,58:444.
[13]Suzuki I,Masuko N,Hisamatsu Y.Electrochemicalproperties of iron rust[J].Corrosion Science,1979,19:521.
[14]Yuantai Ma Ying Li Fuhui Wang,The effect ofα-FeOOH on the corrosion behavior of low carbon steelexposed in tropic marine environment[J].MaterialsChemistry and Physics,2008,112:844-852.
[15]He Jianxin(何建新),Qin XiaoZhou(秦晓洲),Studyon the exposure tests of Q235 steel in coastal atmos-pheric corrosion[J].Surface Technology(in Chi-nese),2006,35(4)21-24.
[16]Han W,Yu G C,Wang Z Y.Characterisation of ini-tial atmospheric corrosion carbon steels by field expo-sure and laboratory simulation[J].Corrosion Science,2007,49:2920-2935.
[17]Ke Wei(柯伟),Summary report on the NSFC project(国家自然科学基金重大项目课题结题报告):"Corrosion in natural environments and predication ofcorrosion behavior",NSFC,Beijing,2009.
[18]Cao C N(曹楚南).Materials corrosion in natural en-vironment of China[M].Bejing:Chemical IndustryPress,2005.2-6,15.