利用"活性"与"非活性"硅烷化学改性环氧涂层以提高其耐蚀性."活性"硅烷指含有可以与环氧树脂的环氧端基发生开环反应官能团的硅烷,通常为氨基硅烷;"非活性"硅烷指不与环氧端基发生反应,但在有机锡催化剂存在下可与环氧树脂骨架上的羟基发生缩合反应的硅烷.红外光谱显示,两类硅烷均可成功接枝在环氧树脂上.电化学阻抗谱(EIS)和加速腐蚀试验(Machu试验)测试表明,经硅烷化学改性后的环氧涂层均能提高其耐蚀性能.
The improvement of corrosion performance of epoxy coatings by modification with "active" and "non-active" silanes is presented."Active" silanes are defined as ones having functional groups that can react with the epoxy groups in the epoxy resin,usually amino-silanes."Non-active" silanes are defined as ones not reacting with the epoxy groups,but can react with the hydroxyl groups in the epoxy backbone by the condensation reactions under the catalysis of organic tin compounds.The FTIR results showed that both the "active" and "non-active" silanes had been successfully grafted onto the epoxy resin.Electrochemical impedance spectroscopy(EIS) and accelerated corrosion test(Machu test) showed that the corrosion performance of epoxy coatings could be improved by chemical modification with both the "active" and "non-active" silanes.
[1]Van Ooij W J,Zhu D,Stacy M,et al.Corrosion pro-tection properties of organofunctional silanes—An over-view[J].Tsinghua Science and Technology,2005,10:639-664.
[2]Liu L(刘倞),Hu J M(胡吉明),Zhang J Q(张鉴清),et al.Progress in anti-corrosive treatment of met-als by silanization[J].Journal of Chinese Society forCorrosion and Protection,2006,26:59-64.
[3]Subramanian V,van Ooij W J.Silane based metal pre-treatments as alternatives to chromating[J].SurfaceEngineering,1999,15:168-172.
[4]Sundararajan G P,van Ooij W J.Silane based pretreat-ments for automotive steels[J].Surface Engineering,2000,16:315-320.
[5]van Ooij W J,Zhu D Q,Prasad G,et al.Silane basedchromate replacements for corrosion control,paint adhe-sion,and rubber bonding[J].Surface Engineering,2000,16:386-396.
[6]Seth A,van Ooij W J.Novel,water-based high-per-formance primers that can replace metal pretreatmentsand chromate-containing primers[J].Journal of Mate-rials Engineering and Performance,2004,13:468-474.
[7]Seth A,van Ooij W J,Puomi P,et al.Novel,one-step,chromate-free coatings containing anticorrosionpigments for metals—An overviewand mechanistic study[J].Progress in Organic Coatings,2007,58:136-145.
[8]Ji W G,Hu J M,Zhang J Q,et al.Reducing the waterabsorption in epoxy coatings by silane monomer incorpo-ration[J].Corrosion Science,2006,48:3731-3739.
[9]Zhu D,van Ooij W J.Corrosion protection of metals bywater-based silane mixtures of bis-[trimethoxysilylprop-yl]amine and vinyltriacetoxysilane[J].Progress in Or-ganic Coatings,2004,49:42-53.
[10]Ji W G,Hu J M,Liu L,et al.Water uptake of epoxycoatings modified withγ-APS silane monomer[J].Progress in Organic Coatings,2006,51:439-443.
[11]Zhang J T,Hu J M,Zhang J Q,et al.Studies of wa-ter transport behavior and impedance models of epoxy-coated metals in NaCl solution by EIS[J].Progress inOrganic Coatings,2004,51:145-151.
[12]Ji W G,Hu J M,Liu L,et al.Improving the corro-sion performance of epoxy coatings by chemical modifi-cation with silane monomers[J].Surface&CoatingsTechnology,2007,201:4789-4795.
[13]Zhou J M,Lucas J P.Hygrothermal effects of epoxyresin.Part II:variations of glass transition temperature[J].Polymer,1999,40:5513-5522.
[14]Fellahi S,Chikhi N,Bakar M.Modification of epoxyresin with kaolin as a toughening agent[J].Journal ofApplied Polymer Science,2001,82:861-878.
[15]Tejedor MI,Raredes L,Anderson MA.Evaluation ofATR-FTIR spectroscopy as an“in situ”tool for follow-ing the hydrolysis and condensation of alkoxysilanesunder rich H2O conditions[J].Chemistry of Materi-als,1998,10:3410-3421.
[16]Ji W G,Hu J M,Liu L,et al.Enhancement of corro-sion performance of epoxy coatings by chemical modifi-cation with GPTMS silane monomer[J].Journal ofAdhesion Science and Technology,2008,22:77-92.
[17]van Ooij W J,Zhu D.Electrochemical impedancespectroscopy of bis-[triethoxysilylpropyl]tetrasulfide onAl 2024-T3 substrates[J].Corrosion,2001,57:413-427.