采用溶胶-凝胶法制备Ti/IrRuSn、Ti/IrTa/IrRuSn和Ti/IrTaSn/IrRuSn氧化物电极,FESEM、XRD观察该电极微观结构,循环伏安、强化电解测试电极电化学性能.结果表明:嵌中间层氧化物电极表面裂纹增多,改变了颗粒形状和平均晶粒尺寸,虽电流效率略有降低,增多活性点,提高电极析氯反应选择性;但2种氧化物电极(Ti/IrTa/IrRuSn和Ti/IrTaSn/IrRuSn)的强化电解寿命和正反交替电解寿命均较好.
Various Ti/IrRuSn,Ti/IrTa/IrRuSn and Ti/IrTaSn/IrRuSn oxide electrodes were prepared by sol-gel method.The surface morphology and microstructure were analysed with FESEM and XRD.The electrochemical activity and stability were investigated using electrochemical technologies including chlorine and oxygen evolving potential measurements,cyclic voltammetry,accelerated life test,and alternative electrolysis.The results indicate that the electrodes with interlayers present more cracks on the surface and a little bigger average grain size,with particles of different shapes precipitated in the cracks.The electroactive sites are increased and the selectivity for the chlorine evolving reaction is enhanced,but the current efficiency for the chlorine production is somewhat lowered by the addition of different interlayers.The stability characterised with accelerated life test and alternative electrolysis of Ti/IrTa/IrRuSn and Ti/IrTaSn/IrRuSn oxide electrodes is significantly higher than Ti/IrRuSn oxide electrode without interlayers.
[1]Wang Bin(王彬),Hou Shizong(侯世忠),Han Yan(韩严),et al.Recent status of development of metaloxide coated anode for antifouling by electrolyzing sea-water[J].Development and Application of Materials(in Chinese),1998,13(1):41.
[2]Wang Juntao(王均涛),Han Yan(韩严),Xu Likun(许立坤),et al.The deactivation mechanism of metaloxide anodes under alternative current electrolysis condi-tion[J].Electrochemistry(in Chinese),2005,11(4):407.
[3]Huang Yuntao(黄运涛),Peng Qiao(彭乔).The de-activation mechanism of metal oxide anode used in sea-water electrolysis[J].Rare Metal Materials and Engi-neering(in Chinese),2006,35(10):1610.
[4]Tang Dian(唐电),Lin Xuan(林萱),Cui Xiong(崔雄),et a1.Design and development of a high perform-ance anode for chlorine-evolution[J].Trans of NonMet(in Chinese),1996,6(1):85.
[5]Wang Lingli(王玲利),Peng Qiao(彭乔).Advancesin research on Ti anodes coating with RuO2[J].Liaoning Chemical Industry(in Chinese),2006,35(8):485.
[6]Ji Lei(嵇雷),Wang Juntao(王均涛),Liu Wenbin(刘文彬),et al.Performance of the Ru-Ir-Sn oxideanode coating influenced by Ru and Sn ratio[J].Elec-trochemistry(in Chinese),2008,14(3):263.
[7]Mraz R,Krysa J.Long service life of IrO2/Ta2O5elec-trodes for electro flotation[J].J of Appl Electrochem,l994,24(12):1262.
[8]Xu L K(许立坤),Scantlebury J D.Microstructure andelectrochemical properties of IrO2-Ta2O5-coated titaniumanodes[J].J Electrochem Soc,2003,150:B288.
[9]Xu L.K(许立坤),Scantlebury J D.A Study on thedeactivation of an IrO2-Ta2O5coated titanium anode[J].Corro Sci,2003,45:2729.
[10]Comninellis C,Vercesi G.Characterization of DSA-type oxygen evolving electrodes:choice of coating[J].J of Appl Electrochem,1991,21:335.
[11]Gong Mingyang(公铭扬).Study on nanostructureIrO2-Ta2O5oxide anode[J].Chinese Coatings(inChinese),2005,20(11):21.
[12]Xu L K(许立坤),Wang J T(王均涛),Xin Y L(辛永磊).Approaches to the performance improvementof metal oxides coated titanium electrode[J].RareMetal Materials and Engineering(in Chinese),2008,37(suppl 3):71.
[13]Chu L Y(初立英),Xu L K(许立坤),Wu L B(吴连波),et al.Effect of oxalic acid etching on morphologyand electrocatalytic activity of oxide anodes[J].ActaMetall Sin(in Chinese),2005,41(7):763.
[14]Xu L K(许立坤),Xin Y L(辛永磊),Wang J T(王均涛).A comparative study on IrO2-Ta2O5coated ti-tanium electrodes prepared with different methods[J].Electrochim Acta,2009,54:1820.
[15]Zhang Fan(张帆),Li Haitao(李海涛).Study on a ti-tanium anode coated with IrO2and amorphous Ta2O5[J].Journal of Guangdong Nonferrous Metals(inChinese),2000,10(1):41.
[16]Lourdes Vazquez-Gomez,Sergio Ferro,Achille DeBattisti.Preparation and characterization of RuO2-IrO2-SnO2ternary mixtures for advanced electrochemicaltechnology[J].Applied Catalysis B:Environmental,2006,67:34.
[17]Morimitsu M,Otogawa R,Matsunaga M.Effects ofcathodizing on the morphology and composition ofIrO2-Ta2O5/Ti anodes[J].Electrochimi Acta,2000,46:401.