PANI/MWCNT电极在硫酸锂溶液中电容性能

  • 丛文博 ,
  • 贺晓书
展开
  • 哈尔滨工程大学材料科学与化学工程学院;

收稿日期: 2009-08-28

  修回日期: 2009-08-28

  网络出版日期: 2009-08-28

Capacitor Property of PANI/MWCNT Electrode in Li_2SO_4 Solution

  • CONG Wen-bo ,
  • HE Xiao-shu
Expand
  • (College of Material Science and Chemical Engineering,Harbin Engineering University,Harbin 150001,China

Received date: 2009-08-28

  Revised date: 2009-08-28

  Online published: 2009-08-28

摘要

化学氧化法制备聚苯胺/多壁碳纳米管复合材料(PANI/MWCNT),扫描电镜(SEM)、XRD及IR表征样品结构及形貌,电化学方法测定复合电极循环伏安曲线、恒流充放电曲线及电极交流阻抗.结果表明,PANI/MWCNT电极在1mol/L的Li2SO4溶液中具有较好电容性能,在电流密度为5mA/cm2时,比电容为412F/g.PANI/MWCNT电极较PANI电极有更好的大电流放电能力,50mA/cm2下复合电极的比电容仍达318F/g,为5mA/cm2时该电极比电容的77.2%,而PANI电极的比电容仅为其5mA/cm2时的56.2%.交流阻抗证明碳纳米管降低复合电极的电阻,显著提高大电流放电能力.

本文引用格式

丛文博 , 贺晓书 . PANI/MWCNT电极在硫酸锂溶液中电容性能[J]. 电化学, 2009 , 15(3) : 288 -292 . DOI: 10.61558/2993-074X.1997

Abstract

Polyaniline/multi-walled carbon nanotubes (PANI/MWCNT) composites synthesized by chemical oxidation method were characterized by scanning electron microscopy (SEM),X-ray diffraction (XRD) and IR techniques. In 1mol/L Li2SO4 neutral solution,the electrochemical performance of the composites electrode was investigated by cyclic voltammetry,galvanostatic charge-discharge tests and ac impedance spectroscopy. The results showed that the composites electrode performed well in 1mol/L Li2SO4 solution,the specific capacitance reached 412F/g at 5 mA/cm2. The composites electrode possessed better capability of high current than that of PANI electrode,the specific capacitance kept at 318 F/g at 50mA/cm2 and was 77.2% of that at 5 mA/cm2,but the specific capacitance of PANI at 50 mA/cm2 was only 56.2% of that at 5 mA/cm2. The addition of multi-walled carbon nanotubes could decrease the resistance of composites electrode,leading to remarkably improve the capability of high current discharge.

参考文献

[1]Ma Renzhi(马仁志),Wei Binqing(魏秉庆),Xu Cai-lu(徐才录),et al.Supercapacitor based on carbon nanotubes[J].Science in China(Series E),2000,30(2):112-116. [2]Sivakkumar S R,Wan Ju Kim.Electrochemical perform-ance of polyaniline nanofibers and polyaniline/multi-walled carbon nanotube composites as an electrode mate-rial for aqueous redox supercapacitors[J].Journal of Power Sources,2007,(171):1062-1068. [3]Vinay Gupta,Norio Miura.Influence of the microstruc-ture on the supercapacitive behavior of polyaniline/sin-gle-wall carbon nanotube composites[J].Electrochemi-cal Acta,2006,(157):616-620. [4]Dong Bin,He Ben-Lin.Preparation and electrochemical characterization of polyaniline/multi-walled carbon nanotubes composites for supercapacitor[J].Materials Science and Engineering,2007,(142):172-176. [5]Hu Chi-Chang,Lin Jeng-Yan.Effects of the loading and polymerization temperature on capacitive performance of polyaniline in NaNO3[J].Electrochemical Acta,2002,(47):4055-4067. [6]Zhou Zhanghua,Cai Naicai.Capacitive of characteris-tics of manganese oxides and polyaniline composite thin film deposited on porous carbon[J].Electrochemical Acta,2005,(94):371-375. [7]Zhang Xiong,Ji Liyan.Synthesis of a novel polyaniline-intercalated layered manganese oxide nanocomposite as electrode material for electrochemical capacitor[J].Journal of Power Sources,2007,(173):1017-1023. [8]Yang Hongsheng(杨红生),Zhou Xiao(周啸),Zhang Qingwu(张庆武).Studies on preparation and proper-ties of polyaniline/fractionized carbon nanotube compos-ites[J].Acta Polymerica Sinica,2004,(5):266-269. [9]Park J H,Park O O.Hybrid electrochemical capacitors based on polyaniline and activated carbon electrodes[J].Journal of Power Sources,2002(111):185-190. [10]Cao Chunan(曹楚南),Zhang Jianqing(张鉴清).An introduction to electrochemical impedance spectroscopy[M].Beijing:Science Press,2002.