以P123为模板剂,软模板法制备出纳米MnO2.酸性条件下引入苯胺并聚合,得到了MnO2/聚苯胺复合材料.X射线衍射(XRD)、红外光谱(IR),扫描电子显微镜(SEM)表征观察样品的结构、形貌.循环伏安、交流阻抗、恒电流充放电等测试MnO2/聚苯胺电极的电化学性能.结果表明:引入苯胺改变了样品纳米MnO2的形貌.MnO2/聚苯胺电极比容量高达190.8F·g-1,500次循环电极比容量仅衰减4.7%,库仑效率均保持在97%以上.
Nano-MnO2 was prepared by using P123 as a soft template.The MnO2 /polyaniline composite was further prepared by polymerization of aniline with the nano-MnO2 in acidic conditions and was investigated by XRD and IR.The morphology of nano-MnO2 observed by SEM was changed with the introduction of aniline.The electrochemical properties of MnO2 /PANI electrode were investigated using cyclic voltammetry,galvanostatic charge-discharge and electrochemical impedance spectroscopy.The specific capacitance of MnO2 /PANI electrode could reach as high as 190.8 F·g-1,which decayed only 4.7% over 500 cycles.And the coulombic efficiency has been maintained at above 97%.
[1]Emerson C Rios,Adriane V Rosario,Regina M Q Mello,et al.Poly(3-methylthiophene)/MnO2composite elec-trodes as electrochemical capacitors[J].Journal of Pow-er Sources,2007,163:1137-1142.
[2]En-Hui Liu,Wen Li,Jian Li,et al.Preparation and char-acterization of nanostructured NiO/MnO2composite e-lectrode for electrochemical supercapacitors[J].Materi-als Research Bulletin,2009,44:1122-1126.
[3]Xiong Zhang,Liyan Ji,Shichao Zhang,et al.Synthesis ofa novel polyaniline-intercalated layered manganese oxide nanocomposite as electrode material for electrochemical capacitor[J].Journal of Power Sources,2007,173:1017-1023.
[4]Zhang Qi-wei(张启卫),Peng Xiao-hong(彭小红),HuangXing-kang(黄行康),et al.Preparation and prop-erties of MnO2/polyaniline composite[J].Chinese Jour-nal of Inorganic Chemistry(无机化学),2008,24(4):600-604.
[5]Sheng yu(生瑜),Chen Jian-ding(陈建定),Zhu De-qin(朱德钦).Polyaniline/nanometer manganese diox-ide composite in-situ oxidation synthesis[J].Journal of Functional Polymers(功能高分子学报),2004,17(1):5-10.
[6]Mao Ding-wen(毛定文),Tian Yan-hong(田艳红).PANI/AC composite for electric double layer capacitors[J].Chinese Journal of Power Source(电源技术),2007,131(8):614-616.