采用阳极氧化和恒电位沉积法制备Pb纳米粒子修饰的多孔Ti基TiO2(Pb/nanoTiO2)膜电极.通过对不同的电沉积电位和时间对比,找出了最佳电沉积条件.SEM分析显示该膜为均匀多孔结构,Pb纳米粒子均匀地分散在TiO2膜的表面.循环伏安和计时电流法研究了L-胱氨酸在Pb/nanoTiO2膜电极上的电催化还原活性,结果表明该电极对L-胱氨酸的还原具有高催化活性和稳定性.
The nanoporous Ti-based TiO2 films electrodes modified with Pb particles(Pb/nanoTiO2) were prepared by using anodization and potentiostatic electro-deposition.The optimum deposition conditions were determined by comparing with various deposition potentials and time.The SEM analyses indicated that the TiO2 films were homogeneous nanoporous structure,and the Pb particles well dispersed on the TiO2 films.The L-cystine electrocatalytic activity reduction on the Pb/nanoTiO2 film electrodes was investigated by cyclic voltammetry and Chronoamperometric curves.The results showed that this type of the electrode posseses high acticity and stability.
[1]Rong Guo,Zhongchun Li,Tianqing Liu.Catalysis of the electrochemical oxidation of L-cysteine by lyotropic me-sophases[J].Colloid Polym Sci,2004,283:243.
[2]LI Zhong-Chun(李中春),LIU Tian-Qing(刘天晴),GUO Rong(郭荣).Electrochemical oxidation of L-cys-teine in sodium dodecyl sulfate admicelles[J].Chinese J Chem,2005,23:404.
[3]Daobao Chu,Mai Xu,Jia Lu,et al.Electrocatalytic re-duction of diethyl oximinomalonate at a Ti/nanoporous TiO2electrode[J].Electrochem Commun,2008,10:350.
[4]Ronan Baron1,AndréDarchen,Didier Hauchard.Elec-trocatalytic reduction of tert-butyl hydroperoxide at iron electrodes[J].Electrochim Acta,2004,49:4841.
[5]Ralph T R,Hitchman M L,Millington J P,et al.The re-duction of L-cystine hydrochloride at lead using static and rotating disc electrodes[J].Electroanal Chem,2005,583:260.
[6]Qingwei Chen,Dongsheng Xu,Zhongyun Wu,et al.Fr-ee-standing TiO2nanotube arrays made by anodic ox-idation and ultrasonic splitting[J].Nanotechnology,2008,19:365708.
[7]Chu C L,Wang R M,Yin L H,et al.Effects of anodic oxidation in H2SO4electrolyte on the biocompatibility of NiTi shape memory alloy[J].Materials Letters,2008,62:3512.
[8]Dae-Jin Yang,Hun Park,Seong-Je Cho,et al.TiO2-na-notube-based dye-sensitized solar cells fabricated by an efficient anodic oxidation for high surface area[J].Jour-nal of Physics and Chemistry of Solids,2008,69:72.
[9]Zhang Bao-cheng(章葆澄).Electroplating technology[M].Beijing:Beijing University of Aeronautics and As-tronautics Press,1993:192-195.
[10]Zheng Huajun,Ma Chunan,Wang Wei,et al.Nanorod tungsten carbide thin film and its electrocatalytic activ-ity for nitromethane electroreduction[J].Electrochem Commun,2006,8:977.
[11]Innocenzo G Casella,Michela Contursi.Electrocatalytic reduction of chlorophenoxy acids at palladium-modified glassy carbon electrodes[J].Electrochim Acta,2007,52:7028.
[12]Chu Dao-bao(褚道葆),Yin Xiao-juan(尹晓娟),Feng De-xiang(冯德香),et al.Electrocatalytic oxidation of ethanol on Pt/nanoTiO2-CNT complex catalysts[J].Acta Phys Chim Sin(物理化学学报),2006,22(10):1241.
[13]Gu Jia-shan(顾家山),Chu Dao-bao(褚道葆),Zhou Xing-fu(周幸福),et al.Heterogeneous electrocatalytic reduction of maleic acid on nanocrystalline TiO2Film modified Ti electrode[J].Acta Chimica Sinica(化学学报),2003,61(9):1405-1409.
[14]Allen J Bard,Larry R Faulkenr.Electrochemical meth-ods fundamentals and applications[M].Beijing:Chem-ical Industry Press,2005.156-177.