Electrochemical Properties of Ni(OH)_2 Doped by NiO

  • CHEN Fei-biao ,
  • WU Bo-rong ,
  • AN Wei-feng ,
  • YANG Zhao-jun ,
  • WU Feng ,
  • CHEN Shi
Expand
  • (School of Chemical Engineering and Environmental Science,Beijing Institute of Technology,Beijing 100081,China

Received date: 2010-02-28

  Revised date: 2010-02-28

  Online published: 2010-02-28

摘要

于Ni(OH)2中添加具有电容特性和大电流充放电性能良好的NiO.研究发现掺杂5%NiO的Ni(OH)2在0.2C倍率下放电容量可达310.1mAh/g,而3C放电容量还可以保持79.5%.其循环伏安扫描氧化还原峰电位差仅为164mV,表明该材料的循环可逆性好.由此可见在Ni(OH)2掺杂适量的NiO,对于Ni(OH)2的大电流充放电性能确有改进作用.

本文引用格式

陈飞彪 , 吴伯荣 , 安伟峰 , 杨照军 , 吴锋 , 陈实 . 掺杂NiO的Ni(OH)_2电化学性能研究[J]. 电化学, 2010 , 16(1) : 39 -42 . DOI: 10.61558/2993-074X.2034

Abstract

The Ni(OH)2 cathode material of MH/Ni was doped by NiO,which behaves as a capacitor and can improve the charge-discharge rate capacity of Ni(OH)2.The electrochemical properties of Ni(OH)2 was characterized by charge-discharge curves and cyclic voltammetry.The results showed that the material had the best discharge property when doped by 5% NiO,and the discharge specific capacity could reach 310.1 mAh/g at 0.2 C rate and remianed 79.5% at 3 C rate.The difference oxidation and reduction potentials between the of the battery was 164 mV when the Ni(OH)2 was doped by 5% NiO,which showed a good cyclic property.

参考文献

[1]Tarascon J M,Armand M.Issues and challenges facing rechargeable lithium batteries[J].Nature,2001,414:359-367. [2]J Van Mierlo,Maggetto G,Lataire P.Which energy source for road transport in the future?A comparison of battery,hybrid and fuel cell vehicles[J].Energy Con-versation&Management,2006,47:2748-2760. [3]Geng M,Northwood D O.Development of advanced re-chargeable Ni/MH and Ni/Zn batteries[J].Int J Hy-drogen Energy,2003;28:633-636. [4]Ross D K.Hydrogen storage:The major technological barrier to the development of hydrogen fuel cell cars[J].Vacuum,2006,80:1084-1089. [5]Graeme A Snook,Noel W Duffy,Anthony G,et al.Eval-uation of the effects of oxygen evolution on the capacity and cycle life of nickel hydroxide electrode materials[J].J Power Sources,2007,168:513-521. [6]Wang X Y,Luo H,Yang H P,et al.Oxygen catalytic e-volution reaction on nickel hydroxide electrode modified by electroless cobalt coating[J].Int J Hydrogen Ener-gy,2004,29:967-972. [7]Deabate S,Fourgeot F,Henn F.Electrochemical behav-iour ofβ(II)-Ni(OH)2/β(III)-NiOOH redox couple upon potentiodynamic cycling conditions[J].Electro-chim Acta,2006,51:5430-5437. [8]Pralong V,Delahaye-Vidal A,Beaudoin B,et al.Electro-chemical behavior of cobalt hydroxide used as additive in the nickel hydroxide electrode[J].J Electrochem Soc,2000,147(4):1306-1313. [9]Elumalai P,Vasan H N,Munichandraiah N.Electroc-hemical studies of cobalt hydroxide-an additive for nick-el electrodes[J].J Power Sources,2001,93:201-208. [10]Ken-ichi Watanabe,Mitsuru Koseki,Naoaki Kumagai.Effect of cobalt addition to nickel hydroxide as a posi-tive material for rechargeable alkaline batteries[J].J Power Sources,1996,53:23-28. [11]Wu Yong(吴勇),Yu Ye-fei(于叶飞),Wu Meng-qiang(吴孟强),et al.Application research of superca-pacitor to automobiles[J].Bus Technology and Re-search(客车技术与研究),2008,(1):11-14.