采用低分子量酚醛树脂/F127混合物填充多孔氧化铝模板孔道,制备了大尺寸介孔孔道、核-壳结构的介孔碳纳米纤维.分别以SEM、TEM及N2等温吸附-脱附观察分析样品形貌和孔结构参数.循环伏安与恒流充放电测定该介孔纳米纤维电极(阳极)的超电容性能.结果表明:介孔碳纳米纤维比电容明显增大,且在高扫速、大电流下具有良好的超电容特性.
Two different mesoporous carbon nanofibers with large mesopore or core-shell structure were prepared by using the resol/F127 mixture to fill the AAO template. The morphology and structural parameters of the samples were characterized by SEM,TEM,and N2 adsorption-desorption analysis. The supercapacitive behaviors of the electrodes were tested by cyclic voltammetry and galvanostatic charge-discharge. The results show that the specific capacitances of mesoporous carbon nanofibers increased obviously and the fine supercapacitive performances were achieved at high scan rate or large current density.
[1]Lee J,Yoon S,Hyeon T,et al.Synthesis of a new meso-porous carbon and its application to electrochemical double-layer capacitors[J].Chem Commun,1999,(21):2177-2178.
[2]Zhou H,Zhu S,Hibino M,et al.Electrochemical capaci-tance of self-ordered mesoporous carbon[J].J Power Sources,2003,122(2):219-223.
[3]Fuertes A B,Pico F,Rojo J M.Influence of pore s-truc-ture on electric double-layer capacitance of template me-soporous carbons[J].J Power Sources,2004,13(2):329-336.
[4]lvarez S,Blanco-López M C,Miranda-Ordieres A J,et al.Electrochemical capacitor performance of mesoporous carbons obtained by templating technique[J].Carbon,2005,43(4):866-870.
[5]Xing W,Qiao S Z,Ding R G.Superior electric double layer capacitors using ordered mesoporous carbons[J].Carbon,2006,44(2):216-224.
[6]Meng Y,Gu D,Zhang F,et al.Ordered mesoporous pol-ymers and homologous carbon frameworks:amphiphilic surfactant templating and direct transformation[J].An-gew Chem Int Ed,2005,44(43):7053-7059.
[7]Meng Y,Gu D,Zhang F,et al.A family of highly or-dered mesoporous polymer resin and carbon structures from organic-organic self-assembly[J].Chem Mater,2006,18(18):4447-4464.
[8]Zhang F,Meng Y,Gu D,et al.A facile aqueous route to synthesize highly ordered mesoporous polymers and car-bon frameworks with Ia3d bicontinuous cubic structure[J].J Am Chem Soc,2005,127(39):13508-13509.
[9]Zhang F,Meng Y,Gu D,et al.An aqueous cooperative assembly route to synthesize ordered mesoporous carbons with controlled structures and morphology[J].Chem Mater,2006,18(22):5279-5288.
[10]Cott D J,Petkov N,Morris M A,et al.Preparation of o-riented mesoporous carbon nano-filaments within the pores of anodic alumina membranes[J].J Am Chem Soc,2006,128(12):3920-3921.
[11]Chae W,An M,Lee S,et al.Templated carbon nanofi-ber with mesoporosity and semiconductivity[J].J Phys Chem B,2006,110(13):6447-6450.
[12]Steinhart M,Liang C,Lynn G W,et al.Direct synthesis of mesoporous carbon microwires and nanowires[J].Chem Mater,2007,19(10):2383-2385.
[13]Wang K,Zhang W,Phelan R,et al.Direct fabrication of well-aligned free-standing mesoporous carbon nanofi-ber arrays on silicon substrates[J].J Am Chem Soc,2007,129(44):13388-13389.
[14]Zheng M B,Cao J M,Ke X F,et al.One-step synthesis of new mesoporous carbon nanofibers through an easy template method[J].Carbon,2007,45(5):1111-1113.
[15]Zheng M B,Ji G B,Wang Y W,et al.A new nano-non-finement effect of hard templates for the shrinkage of mesoporous polymer during carbonization[J].Chem Commun2009,5033-5035.
[16]Li W,Chen D,Li Z,et al.Nitrogen enriched meso-porous carbon spheres obtained by a facile method and its application for electrochemical capacitor[J].Elec-trochem Commun,2007,9(4):569-573.