采用化学镀方法制备三维多孔铜.以其作为集流体,借助电沉积制备三维多孔Sn-Co合金电极.X-射线衍射(XRD),扫描电镜(SEM)分析表明,以多孔铜为集流体制备的SnCo合金电极主要存在CoSn2相和纯Sn相,为三维多孔结构.充放电结果显示,三维结构SnCo合金电极比平面铜集流体上镀得的SnCo合金电极表现出更优越的充放电性能.前者的首次放电(嵌锂)容量为636.3mAh/g,充电(脱锂)容量为528.7mAh/g,首次库仑效率为83.1%,70周后容量为529.5mAh·g-1,保持率为82.6%.此外,还应用电化学阻抗初步研究了三维Sn-Co合金电极在充放电过程发生的嵌脱锂过程.
薛连杰
,
黄令
,
柯福生
,
魏国祯
,
郑小美
,
李君涛
,
樊小勇
. 三维多孔Sn-Co合金负极制备及其电化学性能研究[J]. 电化学, 2010
, 16(2)
: 161
-167
.
DOI: 10.61558/2993-074X.2051
Three-dimensional porous Cu film was prepared by electroless plating,and used as a current collector for preparation of three-dimensional structured SnCo alloy electrode,which was mainly prepared by an electrodeposition method,and composed of pure Sn and CoSn2 phases. Electrochemical experimental results show that three-dimensional structured SnCo alloy electrode exhibits much better cycleability than planar SnCo alloy electrode,with first discharge capacity and charge capacity of 636. 3 and 528. 7 mAh·g-1,respectively. After 70th cycling,capacity retention is 83. 1% with 529. 5 mAh·g-1. The lithiation process during first discharge was investigated by electrochemical impedance spectroscopy
[1]Tarascon J M,Armand M.Issues and challenges facing rechargeable lithium batteries[J].Nature,2001,414:359-367.
[2]Yang J,Takeda Y,Imanishi N,et al.Ultrafine Sn and SnSb0.14powders for lithium storage matrices in lithium-ion batteries[J].Journal of the Electrochemical Socie-ty,1999,146:4009-4013.
[3]Kim H,Cho J.Synthesis and electrochemical properties of Sn87Co13alloys by NaBH4and sodium naphthalenide reduction methods[J].Electrochim Acta,2007,52:4197-4201.
[4]Kepler K D,Vaughey J T,Thackray M M.Copper-tin anodes for rechargeable lithium batteries:an example of the matrix effect in an intermetallic system[J].Journal of Power Sources,1999,(81/82):383-387.
[5]Mukaibo H,Sumi T,Yokoshima T,et al.Electrodeposit-ed Sn-Ni alloy film as a high capacity anode material for lithium-ion secondary batteries[J].Electrochemical and Solid State Letters,2003,6(10):A218-A220.
[6]Tamura N,Fujimoto M,Kamino M,et al.Mechanic sta-bility of Sn-Co alloy anodes for lithium secondary batter-ies[J].Electrochimica Acta,2004,49:1949-1956.
[7]Tamura N Y,Kato A,Mikami Kamino M,et al.Study on Sn-Co alloy anodes for lithium secondary batteries I.A-morphous system[J].J Electrochem Soc,2006,153(8):A1626-A1632.
[8]Tamura N,Kato Y,Mikami A,et al.Study on Sn-Co al-loy anodes for lithium secondary batteries II.Nanocom-posite system[J].J Electrochem Soc,2006,153(12):A2227-A2231.
[9]Huang L(黄令),Jiang H H(江宏宏),Ke F S(柯福生)et.al.Structure and performance of novel three-di-mentional porous Sn-Co negative materials[J].Acta Phys-Chim Sin(物理化学学报),2006,22(12):1537-1541.
[10]Ke F S,Huang L,Wei H B,et al.Fabrication and prop-erties of macroporous tin-cobalt alloy film electrodes for lithium-ion batteries[J].J Power Souces,2007,170:450-455.
[11]Fan X Y,Ke F S,Wei G Z,et al.Sn-Co alloy anode u-sing porous Cu as current collector for lithium ion bat-tery[J].J Alloys and Compounds,2009,476:70-73.
[12]Pereira N,Klein L C,Amatucci G G.Particle size and multiphase effects on cycling stability using tin-based materials[J].Solid State Ionics,2004,167:29-40.
[13]Tamura N,Kato Y,Mikami A,et al.Study on Sn-Co al-loy anodes for lithium secondary batteries I.Amorphous system[J].Journal of the Electrochemical Society,2006,153(8):A1626-A1632.
[14]Dokko K,Fujita Y,Mohamedi M,et al.Electrochemical impedance study of Li-ion insertion into mesocarbon microbead single particle electrode Part II.Disordered carbon[J].Electrochimica Acta,2001,47:933-938.
[15]Umeda M,Dokko K,Fujita Y,et al.Electrochemical impedance study of Li-ion insertion into mesocarbon microbead single particle electrode Part I.Graphitized carbon[J].Electrochimica Acta,2001,47:885-890.
[16]Fan X Y(樊小勇),Zhuang Q C(庄全超),Sun S G(孙世刚),et al.Fabrication and performance of Cu6Sn5alloy anode using porous Cu as current collec-tor[J].Acta Phys Chim Sin,2009(物理化学学报),15:611-616.
[17]Barsoukov E,Kim J H,Kim D H,et al.Parametric a-nalysis using impedance spectroscopy:relationship of between material properties and battery performance[J].Journal of New Materials for Electrochemical Sys-tem,2000,3:301-308.
[18]Larcher D,Beaulieu L Y,Macneil D D,et al.In Situ X-Ray study of the electrochemical reaction of Li withη-Cu6Sn5[J].J Electrochem Soc,2000,147:1658-1662.
[19]Hong J,Wang C S,Kasavajjula U.Kinetic behavior of LiFeMgPO4cathode material for Li-ion batteries[J].Journal of Power Sources,2006,162:1289-1296.
[20]Levi M D,Aurbach D.The application of electroanalyt-ical methods to the analysis of phase transitions during intercalation of ions into electrodes[J].J Solid State Electrochem,2007,11:1031-1042.