应用扫描电子显微镜(SEM)、X射线衍射(XRD)、失重法和电化学方法,研究了硬态铝箔和软态铝箔的成分差别及其腐蚀行为.结果表明,硬态铝箔和软态铝箔在表面形貌、元素成分和晶型结构上均有差异.软态铝箔比硬态铝箔更适合于在低酸度条件下进行腐蚀,这为研发电容器制作工艺的低酸度体系腐蚀提供了参考.
Scanning electron microscopy(SEM),X-ray diffraction(XRD),weight-loss method and electrochemical testing method were employed to study the chemical compositions and corrosion behaviors of hard foil and soft foil.The results showed that the surface morphology,chemical composition and crystal structure of hard foil and soft foil are different.It is found from electrochemical tests that the soft foil is suitable to the corrosion under low acidity conditions,which provides the base for developing the corrosion techniques under low acidity conditions.
[1]Mao W M(毛卫民).Surface microstructure of alumi-num foils for low voltage anode capacitor with high spe-cific capacity[J].World Sci Technol(世界科技与发展),2004,26(3):16-21.
[2]Mao W M(毛卫民),Chen L(陈雷),Sa L M(萨丽曼),et al.Influence of grain boundaries on corrosionstructure of low voltage aluminum foil[J].The ChineseJournal of Nonferrous Metals(中国有色金属学报),2004,14(1):1-5.
[3]Yang B C(杨邦朝),Yu Z(余忠).Study on alterna-ting current etching of low voltage anode foil[J].Elec-tronic Components Materials(电子元件与材料),1998,17(1):9-12.
[4]Feng Z S(冯哲圣),Xiao Z W(肖占文),Yang B C(杨邦朝).Inhibition mechanism of SO4-2in AC.etch-ing of Al-foil[J].Journal of Chinese Society for Corro-sion and Protection(中国腐蚀与防护学报),2003,23(1):70-74.
[5]Chen J J(陈金菊),Feng Z S(冯哲圣),Yang B C(杨邦朝).Comparative research on etched aluminumfoils fabricated by different techniques for aluminum e-lectrolytic capacitor[J].Journal of Functional Materials(功能材料),2005,36(10):1521-1523.
[6]Yan K P(闫康平),Xiang H(向华),Chen S M(陈书明).Effect of initiative pitting of AC.eteching on an-ode aluminm foil[J].Electronic Components Materials(电子元件与材料),1996,15(2):49-51.
[7]Wang G(王刚),Yan K P(闫康平),Yan J X(严季新).The influence of H2SO4/HCl ratio and Al3+con-tent on the tunnel growth of high purity aluminum foil[J].Eletronic Components Materials(电子元件与材料),2003,22(10):10-12.
[8]Gao K Z(高亢之).The survey of aluminum foil for e-lectrolytic capacitor[J].Light Alloy Fabrication Tech-nology(轻合金加工技术),2000,28(11):9-15.
[9]Metikos-Hukovic M,Babic R,Grubac Z.The study of a-luminium corrosion in acidic solution with nontoxic in-hibitors[J].J Appl Electrochem,2002,32:35-41.
[10]Scherer J,Magnussen O M,Ebel T,et al.Initial stagesof the anodic etching of aluminum foils studied by a-tomic force microscopy[J].Corros Sci,1999,41:35-55.