采用电化学沉积技术在3-氨丙基三甲基硅氧烷修饰的多孔氧化铝膜板中制备了具有不同Pt/Ru原子比的双元Pt/Ru阵列纳米管电极（NTAEs）。分别用X-射线衍射和扫描电镜表征了催化剂结构和形态。电化学结果表明：通过控制前驱沉积液的浓度可得到不同PtRu原子比的NTAEs。所制备的Pt 或 Pt/Ru合金阵列纳米电极的真实表面积大，催化活性强，有利于物质传输，对甲醇电氧化显示出显著的催化性能。实验中还系统研究了催化剂组成与CO和CH3OH电催化氧化性能的关系，发现Pt/Ru=50:50的阵列纳米管电极对CO电氧化显示出最好的催化活性；对甲醇电氧化，则Ru原子比为40%的催化剂显示最佳催化性能。

Bimetallic PtRu nanotubes array electrodes (NTAEs) with varied Pt to Ru atomic ratios have been prepared by electrochemical codeposition in 3-aminopropyltri-methoxysilane modified porous anodic alumina (PAA) membranes. The structure and morphology of the catalysts were characterized using X-ray diffraction (XRD) and scanning electron microscopy (SEM), respectively. Electrochemical results showed that the NTAEs with varied atomic ratios could be achieved by controlling the precursor concentration for deposition. The prepared nanoarrays composed of Pt or PtRu alloy promoted the mass-normalized activity toward the sluggish electrooxidation reaction of methanol due to the increased catalytic activity and real surface area, as well as the improved mass transport through the catalysts. Correlations between the anode composition and the electrocatalytic activity of the catalysts toward the electrooxidations of CO and CH₃OH were systemically investigated. The PtRu NTAEs containing ca. 50% Ru showed the highest activity for CO electrooxidation, while the PtRu NATEs of 40% Ru for CH₃OH electrooxidation.