Water-Driven Solid Electrolyte Interphase Governs Continuous-Flow Ammonia Electrosynthesis

Peng-Bo Liu, Sheng-Liang Zhai, Ji Huang, Zhong-Shuo Zhang, Jie Zeng, Shao-Feng Li

Fig. 4. Depth-profile XPS spectra of O 1s (a), Li 1s (b) and F 1s (c) for the SEIs formed under 5-7 mmol·L-1 initial water content and 55-57 mmol·L-1 initial water content. A consistent intensity scale on the y-axis is maintained across all spectra for each sputtering time. XPS analyses were conducted without air exposure. Binding energy scales are adjusted per element to highlight chemical shifts; absolute values are calibrated to adventitious carbon (C 1s at 284.8 eV).