The Electrophoretic Deposition of Nano Hydroxyapatite Coating  on Titanium Surface

Journal of Electrochemistry ›› 2005, Vol. 11 ›› Issue (1): 67-71.

• Articles • Previous Articles Next Articles

The Electrophoretic Deposition of Nano Hydroxyapatite Coating on Titanium Surface

CHEN Fei~1,LIN Chang-jian~

(*1),WANG Zhou-cheng~2(1.State Key Lab for Physical Chemistry of Solid Surfaces,Department of Chemistry, Xiamen University, Xiamen 361005, China,2.Department of Materials Science and Engineering, Xiamen University, Xiamen~()361005, China

Received:2005-02-28 Revised:2005-02-28 Online:2005-02-28 Published:2005-02-28

Abstract

Abstract: A hydroxyapatite coating with nano-structure on the roughened titanium surface was prepared by electrophoretic deposition process. To decrease sintering temperature the HAp nanoparticles synthesizedby a wet chemical method was used. It is observed that the coating is uniform without cracks. After sintering the nano-strueture of HAp coating remains unchanged. The surface treatment of Ti is applied to form a distribution of small pits and TiO_2thin layer that improve the adhesion of coatingto Ti substrate. It is shown that the bonding strength of coating is as high as 18±2.5MPa. The hardness and Young's modulus are 40.6 and 0.42 GPa, respectively.

Key words: Hydroxyapatite, Nano coating, Electrophoretic deposition

CLC Number:

R318.08

CHEN Fei~1,LIN Chang-jian~. The Electrophoretic Deposition of Nano Hydroxyapatite Coating on Titanium Surface[J]. Journal of Electrochemistry, 2005, 11(1): 67-71.

References

[1]　JiH,MarquisPM.Effectofheattreatmentonthemi crostructureofplasma sprayedhydroxyapatitecoating[J].Biomaterials,1993,14:64. [2]　BanS,MarunoS.Effectoftemperatureonelectrochem icaldepositionofcalciumphosphatecoatingsinasimu latedbodyfluid[J].Biomaterials,1995,16:977. [3]　ChaiCS,BenNissanB.Bioactivenanocrystallinesol gelhydroxyapatitecoatings[J].J.MaterSci:MaterMed.,1999,10:465. [4]　YankeeSJ,PletkaBJ,LuckeyHA, etal.Processesforfabricatinghydroxyapatitecoatingsforbiomedicalap plications, thermalsprayresearchandapplication[A].ProceedingsoftheThirdNationalThermalSprayConfer ence[C].California:LongBeach,1990.433. [5]　KnowlesJC,GrossK,BerndeCC, etal.Structuralchangesofthermallysprayedhydroxyapatiteinvestigatedbyrietveldanalysis[J].Biomaterials,1996,17:639. [6]　MaoC,LiH,CuiF, etal.Orientedgrowthofphos phatesonpolycrystallinetitaniuminaprocessmimic kingbiomineralization[J].J.CrystalGrowth,1999,206:308. [7]　SridharTM,MudaliUK,SubbaiyanM.Preparationandcharacterizationofelectrophoreticallydepositedhydroxyapatitecoatingsontype316Lstainlesssteel[J].CorrosionScience,2003,45:237. [8]　DeSenaLA,DeAndradeMC,RossiAM, etal.Hydroxyapatitedepositionbyelectrophoresisontitaniumsheetswithdifferentsurfacefinishing[J].J.BiomedMaterRes.,2002,60:1. [9]　SarkarP,NicholsonPS.Electrophoreticdeposition(EPD): mechanisms[J].Kinetics, andApplicationtoCeramics,J.Am.Ceram.Soc.,1996,79(8):1987. [10]　YeongKCB,WangJ,NgSC.MechanochemicalsynthesisofnanocrystallinehydroxyapatitefromCaOandCaHPO4[J].Biomaterials,2001,22:2705. [11]　KongLB,MaJ,BoeyF.Nanosizedhydroxyapatitepowdersderivedfromcoprecipitationprocess[J].J.Mater.Sci.,2002,37:1131. [12]　NarasarajuTSB,PhebeDE.Review: somephysico chemicalaspectsofhydroxylapatite[J].J.MaterialsScience,1996,31:1. [13]　MalzbenderJ,WithGde.Theuseoftheloadingcurvetoassesssoftcoatings[J].SurfaceandCoatingsTechnology,2000,127:266. [14]　JaeYoungRho,PharrGM.Effectsofdryingonthemechanicalpropertiesofbovinefemurmeasuredbynanoindentation[J].J.Mater.Sci:Mater.Med.,1999,10:485. [15]　RoopKumar,M.Wang.Functionallygradedbioactivecoatingsofhydroxyapatite/titaniumoxidecompositesystem[J].MaterialsLetters,2002,55:133. [16]　WeiM,RuysJ,SwainMV, etal.Interfacialbondstrengthofelectrophoreticallydepositedhydroxyapatitecoatingsonmetals[J].J.MaterSci.MaterMed,1999,10:401.

The Electrophoretic Deposition of Nano Hydroxyapatite Coating on Titanium Surface

PDF (PC)

Knowledge

Abstract

Cite this article

share this article

References

Related Articles 3

Recommended Articles

Metrics

Comments

[1]	GENG Zhi-wang, WANG Hui, LIN Chang-jian. An HAp/nanosilver Coating Prepared by Electrochemical Deposition and its Antibacterial Characterization [J]. Journal of Electrochemistry, 2008, 14(3): 243-247.
[2]	XU Yan-li,LIN Long-xiang,GENG Zhi-wang,LIN Chang-jian*. Electrochemical Codeposition of HA/Collagen Coating and Preliminary in Vitro Tests [J]. Journal of Electrochemistry, 2007, 13(3): 238-241.
[3]	HU Hao_bing,LIN Chang_jian, CHEN Fei, HU Ren, GUO Ming . Pure HAP Film Prepared by Direct Electrodepositing on Metallic Surface and Its Mechanism [J]. Journal of Electrochemistry, 2002, 8(3): 288-294.